SABIC Innovative Plastics LNP STAT-KON MX01767C PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON MX01767C PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* MX01767C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Density | 0.980 g/cc | 0.0354 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | Type I, 5 mm/min; ASTM D638 |
| 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
| 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 18 % | 18 % | 5 mm/min; ISO 527 |
| 25.5 % | 25.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.6 % | 6.6 % | 5 mm/min; ISO 527 |
| 7.5 % | 7.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.57 GPa | 228 ksi | 1 mm/min; ISO 527 |
| 1.76 GPa | 255 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
| Flexural Modulus | 1.49 GPa | 216 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.51 GPa | 219 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.7 J/cm | 27.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 141 kJ/m² | 67.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 32.0 J | 23.6 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 92.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 53.0 °C @Thickness 3.20 mm |
127 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.0 ohm | 3.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering C70H Chloroprene Rubber
- SABIC Innovative Plastics Lexan® HPS6R PC
- Chevron Phillips Xtel® XK2760BL Polyphenylene Sulfide Alloy (discontinued **)
- Borealis HG430MO Polypropylene
- Tra-Con Tra-Bond 221N01
- Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Fabric Form
- EMS-Grivory Grivory® G4V-5H black 9915 PA*-GF50
- ExxonMobil LLDPE LL 3402.48 Blown Linear Low Density Polyethylene Resin
- Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-220 (ISAF)
Copyright © lookpolymers.com All Rights Reserved