- HOME
- POLYMER SEARCH
- Thermoplastic
- Polypropylene (PP)
- Polypropylene with 10% Calcium Carbonate (CaCO3) Filler
- Aclo Accutech Polypropylene Homopolymer HP0334C10L1 Calcium Reinforced
Aclo Accutech Polypropylene Homopolymer HP0334C10L1 Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334C10L1 Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | MD; ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 91 | 91 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ASTM D638 |
| Flexural Strength | 36.0 MPa | 5220 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 0.502 J/cm | 0.940 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.1 °C | 205 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F |
Users viewing this material also viewed the following:
- Polimersan Plastics POLIPOLEN® (Polyethylene) HD-PE 300
- Parker Chomerics CHO-SHIELD® 4997 Part A Conductive Coating
- SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66 (Asia Pacific)
- Sax Polymers SAXLAC 835U Acrylonitrile Butadiene Styrene
- Chase Plastics CP Pryme® N340HSL (COND, 50% RH) Nylon 6 (Utility Grade), 40% Glass Fiber Reinforced, Heat Stabilized, Internally Lubricated
- Eagle Brass 510 Phosphor Bronzes 5% A, Extra Hard
- Diapolyacrylate Acrypet® MF-001 PMMA
- AFE Technologies Cronite 25Cr/12Ni No. HR7
- Polyram PlusTek RA502 Nylon 6.6, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved