- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 73.9 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 73.9 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D-648 |
| Plaskolite Optix® CA - 51 HF OG General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion L0659 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D-648 |
| Plaskolite West Optix® CA - 51 HF OG General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| RheTech Products M40P200-01 40% Mica Reinforced Polypropylene Copolymer, Black Applications: Automotive applicationsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Nilit Polynil® P200 High Viscosity Nylon 66 Description: High viscosityApplication: Semi-finished and FilmInformation provided by NILIT. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Polymer Resources NY6-GP2 General Purpose Nylon 6, Nucleated General Purpose Nylon 6, Nucleated Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Polymer Resources PC/ABS-FR1-[color]-3 PC Blend, Flame Retardant, Standard Flow, UV Stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Dry Blend E7130 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| RheTech Products M25P100-01 25% Mica Reinforced Polypropylene, Black Applications: Underhood applicationsInternal I/P ComponentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Polymer Resources NY66-IM1-[color]-H Nylon 66, Medium Impact Modified, Heat Stabilized Nylon 66, Medium Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Ny.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 - 220 °C | 165 - 428 °F | Average value: 131 °C Grade Count:15 |
| Overview of materials for Nylon 66, Mineral Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, Impact Grade". Each property range of values reported is minimum and maximum v.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed (0.250"); ASTM D648 |
| LTL Color Compounds ColorFast® FRA202 General Purpose ABS General purpose V0/5VA-rated ABSAll information provided by LTL Color Compounders, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| KYDEX® 110 Metallic Thermoplastic Fire-rated Sheet Features:For deep or hard to form parts where good finished detail is requiredMore rigid than most thermoplastics, parts deform less when loadedMeets highest standard for chemical resistance for the.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Fiberfil® PP-60/CC/30 Polypropylene Homopolymer, 30% Calcium Carbonate Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® HDPE 04001 LE BK Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/Reinfor.Features: ESD Protection and ConductiveAppearance: BlackProcessing Method: ExtrusionInformation provided by .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Spartech Royalite R87/59 ABS/PVC Weather Resistant Sheet Description: Weather Resistant SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PA6/6 HS L N Nylon 66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and Nucleating AgentFeatures: Heat Stabilized, Impact Modified and NucleatedProcessing Method: Injection MoldingIn.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PC/ABS FR 6206 UV Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES Statiblend® ABS FR AS BN Availability: North AmericaForms: PelletsAdditive: AntistaticFeatures: Antistatic and Flame RetardantInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6 0254 B Barium Sulfate Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Barium SulfateFeatures: High Specific GravityInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PP GB40 40% Glass Beads Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 40% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM Data |
| Styron Magnum™ 213 ABS, General Purpose MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Westlake Plastics HIPS High Impact Polystyrene, Compression Molded Compression molded HIPS is a low cost plastic material that is easily machined and fabricated. It is frequently used for preproduction prototyping. HIPS is a FDA compliant use in food processing a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Westlake Plastics HIPS High Impact Polystyrene HIPS is a low cost plastic material that is easy to machine and fabricate. It is often specified for low strength structural applications when impact resistance, machinability, and low cost are req.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0334M30CL Mica Reinforced Coupled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® UR-20GF/000 Thermoplastic Elastomer - TPU, Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||