PolyOne Edgetek® UR-20GF/000 Thermoplastic Elastomer - TPU, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® UR-20GF/000 Thermoplastic Elastomer - TPU, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 46.9 MPa | 6800 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 1.24 GPa | 180 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 41.4 MPa | 6000 psi | ASTM D790 |
| Flexural Modulus | 1.03 GPa | 150 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
10.0 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 216 °C | 380 - 420 °F | Molding |
| Mold Temperature | 15.6 - 37.8 °C | 60.0 - 100 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets | |
| Rockwell Hardness | 65 D | ASTM D785 |
Users viewing this material also viewed the following:
- Sharadaa Ceramics ZAP 013 Smart Cast Application
- Schmolz + Bickenbach UGICHROM 4542 Martensitic Chrome Plated Bar
- Teknor Apex Telcar® TL-1120E Thermoplastic Elastomer
- DSM Arnite® BM4 240 (PBT+PET)-MD20
- ExxonMobil Vistalon™ 722 Ethylene Propylene Copolymer Rubber - Wire and Cable
- Dow DOWLEX™ 2244A Linear Low Density Polyethylene, Cast Film Grade
- PolyChem Alloy PolySept 2006
Copyright © lookpolymers.com All Rights Reserved