PolyOne Geon™ Vinyl Rigid Extrusion L0659 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L0659 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 42.3 MPa | 6140 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 3.27 GPa | 474 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 80.6 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 3.21 GPa | 466 ksi | ASTM D790 |
| Izod Impact, Notched | 1.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.44 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A |
| 1.40 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.62 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| 11.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
20.6 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 38.3 J/cm @Temperature 23.0 °C |
0.0718 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 43.1 J/cm @Temperature 23.0 °C |
0.0807 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | All Colors |
| V-0 @Thickness 0.711 mm |
V-0 @Thickness 0.0280 in |
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Features | General Purpose | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 16364 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | General Purpose | |
| Profiles |
Users viewing this material also viewed the following:
- Fainplast Compounds RE 612 Rigid PVC, Extrusion
- H.C. Starck NRC® 4N5 (UNS R05200) Electron Beam Melted Tantalum
- SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC (Asia Pacific)
- A. Schulman POLYBATCH™ Red 5505 Concentrate Based In Polyethylene
- EMS-Grivory Grivory® HTV-45H1 black 9205 PA6T/6I-GF45
- Dow DMDA-8907 NT 7 High Density Polyethylene Resin
- Eurostar Starflam PX06009 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- BNZ Materials BNZ-26-60 Insulating Firebrick
- Arlon LW401B##-P2 0.040" (1.02 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Alliance BIN-72 Bonded (Composite) Magnetic Material
Copyright © lookpolymers.com All Rights Reserved