Techmer ES HiFill® PP GB40 40% Glass Beads Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Glass Bead Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PP GB40 40% Glass Beads Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 40% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ASTM D785 |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Yield Strength | 31.0 MPa | 4500 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.17 mm |
0.600 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C | 35.0 µin/in-°F | ASTM D696 |
| Melting Point | 170 °C | 338 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C6840 PC+ABS (Asia Pacific)
- Solvay Specialty Polymers KetaSpire® KT-850P Polyetheretherketone (PEEK) (Unverified Data**)
- Schott Glass 8230 Intermediate sealing glass
- Techmer ES Electrafil® J-1200/CF/30 ABS, 30% Carbon Fiber Reinforced
- DAK Americas Laser+® B90A PET
- DuPont Teijin Films Mylar® OL2 Polyester Film, 50 Gauge
- Bhansali Engineering Abstron HI-40 ABS High Impact Injection Molding
- BLUESTAR PBT 1100
- Borealis Visico™/Ambicat™ LE4423/LE4476 Fast Curing, Easy Processing, Environmentally Friendly, Silane Crosslinkable LDPE Compound for Low Voltage Insulation
Copyright © lookpolymers.com All Rights Reserved