- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 246 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 246 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Polymer Resources NY66-FRG25 Flame Retardant Nylon 66, 25% Glass Reinforced Nylon 66, 25% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Polymer Resources NY66-G20-MD Nylon 66, 20% Glass Reinforced with MoS2 Nylon 66, 20% Glass Reinforced with Molybdenum Disulfide for Lubrication and WearProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigment.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Polymer Resources NY66-IM2-G33 Nylon 66, 33% Glass Reinforced, Impact Modified Nylon 66, 33% Glass Reinforced, Impact Modified, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Polymer Resources NY66-IM2-G33-[color]-H Nylon 66, 33% Glass Reinforced, Impact Modified, Heat Stabilized Nylon 66, 33% Glass Reinforced, Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Polymer Resources NY66-IM-G40 Nylon 66, 40% Glass Reinforced, Impact Modified Nylon 66, 40% Glass Reinforced, Toughened and LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon g.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1025HLFR Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 - 255 °C | 475 - 491 °F | Average value: 249 °C Grade Count:3 |
| Overview of materials for Nylon 63, 35% Glass-Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 63, 35% Glass-Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Solvay TECHNYL® A 60 G1 V25 PA66, 25% glass fiber, DRY Description: TECHNYL® A 60G1 V25 is a 25% GF reinforced organophosphorous flame retarded grade based on a patented high flow polyamide 66 resin. This product is heat stabilized and provides optim.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006L PA 66 (Asia Pacific) LNP* Thermocomp* RF006L is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 LNP* THERMOCOMP* RF006LXP is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 LNP* THERMOCOMP* RF006S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp RF00ASXP PA6.6 (Europe-Africa-Middle East) LNP* THERMOCOMP* RF00ASXP is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Techmer ES Plaslube® J-1/CF/10/TF/13/SI/2 NAT PA66 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN133GL (COND, 50% RH) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN133GLUV (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated, UV Stabilized Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ISO 75-1/-2 |
| DSM Akulon® M-1016 (Dry) 33% Glass Reinforced Nylon 66 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
| Eurostar Staramide AG5K PA66, 25% Glass Filled, Injection Molded AG5 is a Heat and Hydrolytically Stabilized, 25% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppli.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Adell AL-38 Nylon 66, 40% Glass Reinforced; Mineral Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Ashley Polymers Ashlene® 541-25G Nylon 66, 25% Glass Reinforced Nylon 66, 25% glass reinforced for extrusion applications.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Adell AJ-37 Nylon 66, 35% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Adell AT-17 Nylon 66, 35% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Unannealed; ASTM D648 |
| Teknor Apex Chemlon® 109-33 GH Nylon 66, 33% Glass Fiber Filled Notes: High-Impact; Reinforced with 33% Glass Fibers; Highly toughened compound exhibiting strength and rigidity Features: Good Creep Resistance; Good Stiffness; High Strength; Good Impact Resistanc.. |
|||