- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 213 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 213 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ISO 75, ASTM D648 |
| Nilit Nilamid B3 H G8 40% Glass Fiber Reinforced PA6 Description: Nilamid B3 H G8 is a product that combines outstanding strength and stiffness with good moldability and good impact strength. It is widely used for structural applications.Key character.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.18 mm |
415 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne Edgetek® RA-10GF-10CF/000 HI Polyphenylsulfone (PPSU) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced
(discontinued **) Description/Features:Carbon Fiber ReinforcedInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ISO 75-1, -2 |
| Lanxess Durethan® DP BKV 60 EF 000000 Nylon6, 60% Glass Fiber PA 6, 60% glass fibers, injection molding, improved flowabilityInformation provided by LANXESS. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF30 IM L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedUL File N.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF33 IM L 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedUL File N.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF40 IM HS UV RD 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedUL File Number: E157318Processing Meth.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT (Asia Pacific) LNP LUBRICOMP* WFP36 is a compound based on Polybutylene Terephalate resin containing Silicone, Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Kalix® 2855 Polyamide, High Performance (HPPA), Glass Fiber Kalix® 2855 is a 27% bio-sourced, PA 6,10-based compound with 55% by weight glass fiber reinforcement. This material is formulated to provide maximum strength, stiffness, impact resistance, and p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6 GF50 IM L NAT002 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP EC002XXQ PEI LNP* THERMOCOMP* EC002XXQ is a compound based on Polyetherimide containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Techmer ES Plaslube® J-3/30/TF/15 Nylon 6, 30% GFR, 15% PTFE Plaslube glass fiber reinforced polytetrafluoroethylene (PTFE) lubricated nylon 612 grades offer a unique balance of excellent wear and friction performance with good dimensional stability and mecha.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PET GF/M40 BK 40% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP QF00A PA6.10 LNP* THERMOCOMP* QF00A is a compound based on Nylon 6/10 containing 50% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Verton PV00A PA 6 (Europe-Africa-Middle East) LNP* Verton* PV00A is a compound based on Nylon 6 resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Unitika RUN35-C25 Weather resistant PA6, Dry Weather resistant, noncoating, external exposure-compatibleInformation provided by Unitika Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 213 °C | >= 415 °F | ISO 75 Af |
| Vyncolit A2710 Glass Fiber Reinforced Novolac Phenolic Vyncolit A2710 is a glass fiber reinforced phenolic molding compound with excellent mechanical and thermal properties.Information provided by Sumitomo Bak North America, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | dry; ISO 75-1/-2 |
| DSM Novamid® 1010GN2-30 NAT/BK37 PA6-GF30 FR(17) 30% Glass Reinforced, Flame Retardant |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM Test |
| BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Dry) Ultramid HMG13 HS BK-102 is a 63% glass filled, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldabil.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Asahi Kasei Thermylon® NSG-240A 50% Ceramic and Glass Fiber Reinforced Information provided by Asahi Thermofil |
|||