Vyncolit A2710 Glass Fiber Reinforced Novolac Phenolic
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled |
| Manufacturer | Vyncolit N.V., Sumitomo Bakelite |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Vyncolit A2710 Glass Fiber Reinforced Novolac Phenolic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vyncolit A2710 is a glass fiber reinforced phenolic molding compound with excellent mechanical and thermal properties.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | ISO 60 |
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Water Absorption | 1.81 % | 1.81 % | ISO 62 |
| Linear Mold Shrinkage | 0.0041 cm/cm | 0.0041 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | ISO 527-1 |
| Elongation at Break | 0.57 % | 0.57 % | ISO 527-1 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527-1 |
| Flexural Strength | 168 MPa | 24400 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Compressive Strength | 242 MPa | 35100 psi | ISO 604 |
| Charpy Impact Unnotched | 1.17 J/cm² | 5.57 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.290 J/cm² | 1.38 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | TMA |
| CTE, linear, Transverse to Flow | 52.0 µm/m-°C | 28.9 µin/in-°F | TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 213 °C | >= 415 °F | ISO 75 Af |
| Shrinkage | 0.11 % | 0.11 % | Post Shrinkage; ISO 2577 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Molding Method | Compression | |
| Injection | ||
| Transfer |
Users viewing this material also viewed the following:
- Polimeri Europa Edistir ICE R 830D Polystyrene
- Gouda Vuurvast CURAS 40 Moldable Refractory Material
- Mitsui Arlenâ„¢ C215 15% Glass Fiber-Reinforced Modified Nylon 6T (COND)
- Isoflon PUR Polyurethane
- Total PS CPDS 801 Flame Retardant Polystyrene
- ExxonMobil Label-Lyte™ 50LH247 OPP Film
- DuPont Teijin Films Teijin® Tetoron® G2 Polyester Film, 150 Gauge
- A. Schulman POLYBATCH™ White 8350/UV5 Concentrate Based In Polyethylene
- PolyOne Edgetek® AM-20CF-20GF/000 Polyphthalamide (PPA), Glass/Carbon Fiber Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved