SABIC Innovative Plastics LNP THERMOCOMP QF00A PA6.10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP QF00A PA6.10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* QF00A is a compound based on Nylon 6/10 containing 50% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.210 % | 0.210 % | 50% RH, 24 hrs; ASTM D570 |
| 0.280 % | 0.280 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0018 - 0.0020 cm/cm @Time 86400 sec |
0.0018 - 0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.015 cm/cm @Time 86400 sec |
0.0050 - 0.015 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 181 MPa | 26300 psi | Type I, 5 mm/min; ASTM D638 |
| 181 MPa | 26300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 181 MPa | 26300 psi | Type I, 5 mm/min; ASTM D638 |
| 181 MPa | 26300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 15.51 GPa | 2250 ksi | 1 mm/min; ISO 527 |
| 18.68 GPa | 2709 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 285 MPa | 41300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 280 MPa | 40600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.44 GPa | 1659 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.87 GPa | 1867 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.05 J/cm | 24.45 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 1.50 µm/m-°C @Temperature -40.0 - 40.0 °C |
0.833 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 7.83 µm/m-°C @Temperature -40.0 - 40.0 °C |
4.35 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Network Polymers Kepital® F20-03
- Albis Plastics Cellulose Acetate Butyrate B9025 , 8% Plasticizer (discontinued **)
- Teknor Apex Monprene® MP-1855PV2 Thermoplastic Elastomer
- TriStar TriSteel AC Metal Backed PTFE Bearing System
- Fainplast Compounds PHS 60 Flexible PVC, Transparent Extrusion
- 3M Dyneon™ FPO 3740 Fluoroelastomer
- Azoty Tarnow™ Tarnamid® T-27 GF20 GB10 Polyamide 6 - Glass Beads Reinforced
- Asahi Kasei Thermylene® P6-30FG-0709 30% Fiber Glass Reinforced, Heat Stabilized
- MV Labs RH465 Na3RhCl6 Sodium hexachlororhodate(III)
- ExxonMobil Oppalyte™ 30 HM-3 OPP Film
Copyright © lookpolymers.com All Rights Reserved