DSM Novamid® 1010GN2-30 NAT/BK37 PA6-GF30 FR(17)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1010GN2-30 NAT/BK37 PA6-GF30 FR(17).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Flame Retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.70 % | 1.70 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | cond; ISO 527-1/-2 |
| 160 MPa | 23200 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 1.7 % | 1.7 % | dry; ISO 527-1/-2 |
| 2.6 % | 2.6 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 8.30 GPa | 1200 ksi | cond; ISO 527-1/-2 |
| 12.1 GPa | 1750 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 200 MPa | 29000 psi | cond; ISO 178 |
| 260 MPa | 37700 psi | dry; ISO 178 | |
| Flexural Modulus | 8.30 GPa | 1200 ksi | cond; ISO 178 |
| 11.5 GPa | 1670 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 5.40 J/cm² @Temperature 23.0 °C |
25.7 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 6.40 J/cm² @Temperature 23.0 °C |
30.5 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Glow Wire Test | 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.00e+14 ohm-cm | 6.00e+14 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 5.0 @Frequency 100 Hz |
5.0 @Frequency 100 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.013 @Frequency 100 Hz |
0.013 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 225 V | 225 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- Hybrid Plastics POSS® EP 1050 Epoxy Adhesive
- LG Chemical LUPOL TE5107 PP+Rubber+MF, High Impact
- Sibur SKI-3S Superior Quality, 2nd Group Isoprene Rubber (IR)
- Borealis Borecene Compact™ RM7406 Black Metallocene Linear Polyethylene for Rotational Molding
- UBE UBEPOL VCR412 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Dow Corning 752 ADHESIVE/SEALANT
- Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes
- Polymer Resources PPX/NY GP1 Modified PPO, General Purpose PPX/Nylon 6,6 Alloy (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved