BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid HMG13 HS BK-102 is a 63% glass filled, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldability and outstanding surface appearance.
Physical Properties Metric English Comments
Density 1.74 g/cc
0.0629 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 207 MPa
30000 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 245 MPa
35500 psi
5mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5mm/min; ISO 527
3.0 %
3.0 %
0.2 in/min; ASTM Test
Tensile Modulus 22.4 GPa
3250 ksi
1mm/min; ISO 527
Flexural Strength 355 MPa
51500 psi
ISO Data
378 MPa
54800 psi
ASTM Test
Flexural Modulus 17.3 GPa
2510 ksi
ASTM Test
18.0 GPa
2610 ksi
ISO Data
Izod Impact, Notched 1.55 J/cm

@Thickness 3.17 mm
2.90 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Unnotched 13.88 J/cm
26.00 ft-lb/in
ASTM Test
Izod Impact, Notched (ISO) 12.5 kJ/m²
5.95 ft-lb/in²
ISO Test
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 213 °C
415 °F
ASTM Test
214 °C
417 °F
ISO 75
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
UL.UL-C Yes