- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 414 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 414 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.18 mm |
414 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne LubriOne™ NL-30CF/15T Black Polyamide 612 (Nylon 612) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.18 mm |
414 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne LubriOne™ NL-30GF/15T Black Polyamide 612 (Nylon 612) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.18 mm |
414 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ GF 600 A 14 Natural Polyamide 6 (Nylon 6) The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ISO 75-1,-2 |
| Gromax BFG30-FH00N1 Nylon 6 30% Glass Filled (Conditioned) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ISO 75-1, -2 |
| Lanxess Durethan® DP A 30 S FN30 DUS025 000000 Nylon 66 PA 66, non-reinforced, injection molding, halogen free flame retardant improved flowabilityInformation provided by LANXESS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | DIN 53461; ASTM D648 |
| Kolon KOPA® KN133G50 G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 LNP* LUBRICOMP* IFL34 is a compound based on Nylon 6/12 resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 LNP* LUBRICOMP* IFL34 is a compound based on Nylon 6/12 resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 (Asia Pacific) LNP* Lubricomp* IFL34 is a compound based on Nylon 6/12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 2300 PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification, KTW certification in recognized colors. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 2300R PEI 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 2410EPR PEI (Asia Pacific) 40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 2410EPR PEI (Europe-Africa-Middle East) 40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. Resin is RoHS compliant. UL94 V0 listing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics ULTEM AR9300 PEI (Europe-Africa-Middle East) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 420SE0U PBT PBT, 30% Glass Reinforced, Flame Retardant UL94 V-0/5VA rated, UV-Stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 865 PBT+PET 30% GR PBTP, UL94 V-0 rated. Non-blooming flame retardant. Improved surface appearance. Same application areas as for VALOX 855. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PES GF20 TL15 LE 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightPTFE LubricantFeatures: Low Extractables and LubricatedInformation provided by TP Compos.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES LNP* THERMOCOMP* JF003XXZ is a compound based on Polyethersulfone resin containing 15% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 (Europe-Africa-Middle East) Noryl GTX GTX977 resin is a mineral reinforced conductive Noryl GTX with a improved CTE (7) with a balanced performance of Impact and stiffness. (developmental grade : EXNX0074)This data was supplie.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON PV007 PA 6 LNP* VERTON* PV007 is a compound based on Nylon 6 resin containing 35% Long Glass Fiber. Added feature of this grade is: Structural. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ASTM D648 |
| Westlake Plastics Tempalux® 30% GF Polyetherimide An amorphous thermoplastic polyetherimide, stock shapes from ULTEM® resin possess a combination of useful characteristics, including high strength at elevated temperatures, high modulus, and broad .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | 1/4''; ASTM D648 |
| Ensinger TECAPEI® 30% Glass Reinforced, made from Ultem® 2300 PEI TECAPEI™ is an amorphous thermoplastic polyetherimide (PEI) made from Sabic Innovative Plastics' Ultem® 1000 and 2000 series resins. The unreinforced 1000 series materials are translucent amber in.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf |
| Eurostar Staramide BG3 PA6, 15% Glass Filled, Injection Molded BG3 is a 15% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ASTM D648 |
| Beijing Ranger Chem PBT-MFC-G20 FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | |
| Arkema Group Orgalloy® R 6030 Nylon 6 Alloy, 30% Glass fiber (Conditioned) Rigid polyamide 6 alloy: easy to process, low moisture absorption, chemical resistance (no known solvents).Special 30% glass fiber reinforced for overmolding with modified PP.ISO data provided by th.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ASTM D648 |
| Beijing Ranger Chem PBT-201-G20 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ASTM D648 |
| BLUESTAR 201-G20202 PBT, 20% Glass Filled Typical Applications: Energy saving lighting, E/E applicationsInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf |
| Eurostar Staramide BG3H PA6, 15% Glass Filled, Injection Molded BG3H is a Heat Stabilized, 15% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||