SABIC Innovative Plastics ULTEM 2300 PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 2300 PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification, KTW certification in recognized colors.
Physical Properties Metric English Comments
Specific Gravity 1.51 g/cc
1.51 g/cc
ASTM D792
Water Absorption 0.16 %

@Time 86400 sec
 0.16 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.90 %
0.90 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 5.0 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 5.0 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 114
114
ASTM D785
Tensile Strength at Break 158 MPa
22900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 168 MPa
24400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 9.30 GPa
1350 ksi
5 mm/min; ASTM D638
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 8.96 GPa
1300 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
4.91 J/cm

@Thickness 3.20 mm
 9.20 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Izod Impact, Unnotched 4.27 J/cm
8.00 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.8 µm/m-°C

@Temperature -20.0 - 150 °C
 11.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 212 °C

@Thickness 6.40 mm
 414 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 227 °C
441 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 180 °C
356 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 180 °C
356 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.250 mm
 V-0

@Thickness 0.00984 in
 UL 94
5VA

@Thickness 1.21 mm
 5VA

@Thickness 0.0476 in
 UL 94
Oxygen Index 50 %
50 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+16 ohm-cm
3.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.7

@Frequency 1000 Hz
 3.7

@Frequency 1000 Hz
 ASTM D150
Dielectric Strength 24.8 kV/mm

@Thickness 1.60 mm
 630 kV/in

@Thickness 0.0630 in
 in air; ASTM D149
30.3 kV/mm

@Thickness 1.60 mm
 770 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
Dissipation Factor 0.0015

@Frequency 1000 Hz
 0.0015

@Frequency 1000 Hz
 ASTM D150
0.0053

@Frequency 2.45e+9 Hz
 0.0053

@Frequency 2.45e+9 Hz
 ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
NBS Smoke Density, Flaming, Ds 4 min 1.6
ASTM E 662