SABIC Innovative Plastics ULTEM AR9300 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM AR9300 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 160 MPa | 23200 psi | ISO 2039-1 |
| Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.50 GPa | 1380 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 225 MPa | 32600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature 23.0 - 150 °C |
9.44 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature 23.0 - 150 °C |
23.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 210 °C | 410 °F | Rate B/50; ISO 306 |
| 215 °C | 419 °F | Rate B/120; ISO 306 | |
| 220 °C | 428 °F | Rate A/50; ISO 306 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
| OSU total heat release (2 minute test) | 5kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 40kW/m^2 | FAR 25.853 |
Users viewing this material also viewed the following:
- Microtherm Group Molded Pipe Sections Filament Reinforced Silica Pipe Insulation
- Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
- MRC Polymers NAXALOYâ„¢ 770-BK272 ABS + PC Alloy
- Sylvin Technologies 5131-80 PVC Wire/Cable Compound
- Master Bond FL901S Silver Filled, Electrically Conductive Adhesive Film
- Epoxy Technology EPO-TEK® 301-2FL Low Stress, Optical Epoxy
- Ashley Polymers Ashlene® P266 PPO, 30% Glass Reinforced
- Beijing Chemical Industry KAIFA® 301-G15 PBT Resin
- Permabond HM135 Anaerobic Retainer
Copyright © lookpolymers.com All Rights Reserved