- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 244 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 244 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.18 mm |
244 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ PPC-20T Nat Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.18 mm |
244 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ STFPP.1220 BK-L Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.18 mm |
244 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Trilliant™ HC X HC5200-0025 RS Natural Polypropylene Copolymer (PP Copolymer) Information provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CS9610 PC+ABS (Europe-Africa-Middle East) Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYlux 104 HF PC/PBT-Blend, High Flow Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T15020 H4 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T16020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | |
| Covestro Bayblend® KU 2-1446 Polycarbonate + ABS Blend
(discontinued **) Key Features:UnfilledPlatableSuitable processing methods:Injection moldingFilm extrusionProfile extrusionSheet extrusionBlow moldingInformation provided by Bayer Polymers.As of 1 September 2015, Bay.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| BP Amoco Acctuf® 3119HS Ultra High Impact Copolymer Polypropylene
(discontinued **) Suggested fabrication methods: Extrusion; ThermoformingFeatures: High stiffness, Low Temperature impactComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from inject.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 6.40 mm |
244 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical XR474 ABS, Heat Resistance Feature: Injection Molding, Heat ResistanceApplication: Automotives Interior & Exterior HousingCAS No. 25120-20-1, 9003-56-9, 31621-07-5, and 9003-54-7Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | Unannealed; ASTM D648 |
| LyondellBasell Pro-faxâ„¢ SC204 Polypropylene Copolymer Description: Pro-faxâ„¢ SC204 polypropylene copolymer resin is designed for thermoforming and sheet extrusion applications. It is nucleated and features antistatic properties. Pro-faxâ„¢ SC20.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-1120 AN 20% Talc-Filled Polypropylene Homopolymer INNOPOL® CS 1-1120 AN is a 20% talc-filled polypropylene homopolymer compound /PP-H TD20 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 1-1120 AN is develo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON FX98501 PE LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xylex FXY391DF PC+POLYESTER (Asia Pacific) PC+Polyester alloy in Diffusion Visual fx. This grade is compliant with US FDA/European food contact regulations. Color package may influence performance.This data was supplied by SABIC-IP for the A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 6.40 mm |
244 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM3020 PPE+HIPS (Europe-Africa-Middle East) LNP* Thermocomp* Noryl_FM3020 compound is GR/MR 30%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 6.40 mm |
244 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM3020 PPE+PS LNP* Thermocomp* Noryl_FM3020 compound is GR/MR 30%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PX2637 PPE+HIPS (Asia Pacific) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-2 |
| Borealis Bormod™ HC905TF Polypropylene Homopolymer for Thermoforming Bormod HC905TF is a low melt flow rate polypropylene homopolymer intended for thermoformed packaging applications. This homopolymer is produced using the Borealis Controlled Crystallinity Polypropy.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1666 is a 10% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1666 is a 10% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-2/B |
| ExxonMobil Exxtral™ HMU 216 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin characterized by high stiffness and designed for automotive exterior applications in which good surface finish and good UV resistance .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-1/-2 |
| Covestro Bayblend® KU 1-1446* Polycarbonate + ABS Developmental productGrade with improved low-temperature impact strength and petrol resistance for automotive partsin version BBS904 suitable for extrusion/extrusion blow molding and electroplating .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Adell EA-14 Homopolymer Polypropylene, 20% Talc Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Samyang Triel® 5700 Thermoplastics Polyetherester Elastomer, General Extrusion Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5700 is an extrusion grade.Information provided by Samyang. |
|||