Inno-Comp INNOPOL® CS 1-1120 AN 20% Talc-Filled Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-1120 AN 20% Talc-Filled Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 1-1120 AN is a 20% talc-filled polypropylene homopolymer compound /PP-H TD20 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 1-1120 AN is developed for producing injection molded components.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc @Temperature 23.0 °C |
0.0376 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 230 °C |
22 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527-1,-2 |
| Elongation at Yield | 4.2 % | 4.2 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.75 GPa | 399 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 1.50 J/cm² @Temperature -20.0 °C |
7.14 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eU |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.130 J/cm² @Temperature -20.0 °C |
0.619 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 0.230 J/cm² @Temperature 23.0 °C |
1.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-1,-2 |
| Vicat Softening Point | 95.0 °C | 203 °F | B120; ISO 306 |
| 152 °C | 306 °F | A120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8802 BLK
- Plastcom SLOVALEN PC 71 GF 10 PP, 10% glass fibre
- Glastic 4640-15 Fiberglass-Reinforced Polyester Standoff Insulator
- Kotec Carbotex K-30FRT12 Polycarbonate, Flame Retardant
- Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant
- Shin-Etsu Silicones KM-9735 Fluid
- Borealis Xmod™ GD301FE Polypropylene, Glass Fiber Reinforced
- 3M 1000 NS Fire Barrier Water Tight Sealants
- Asahi Kasei Tenac® GA520 Homopolymer Acetal Resin
- Teknor Apex Sinvicomp SBB 3710 Polyvinyl Chloride, Rigid
Copyright © lookpolymers.com All Rights Reserved