Samyang Triel® 5700 Thermoplastics Polyetherester Elastomer, General Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5700 Thermoplastics Polyetherester Elastomer, General Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5700 is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 6.0 g/10 min @Load 2.16 kg, Temperature 240 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength, Ultimate | 39.2 MPa | 5690 psi | ASTM D638 |
| Tensile Strength, Yield | 23.5 MPa @Strain 5.00 % |
3410 psi @Strain 5.00 % |
ASTM D638 |
| 25.3 MPa @Strain 50.0 % |
3670 psi @Strain 50.0 % |
ASTM D638 | |
| 27.9 MPa @Strain 10.0 % |
4050 psi @Strain 10.0 % |
ASTM D638 | |
| Flexural Yield Strength | 24.5 MPa | 3560 psi | ASTM D790 |
| Flexural Modulus | 0.608 GPa | 88.2 ksi | ASTM D790 |
| Izod Impact, Notched | 0.686 - 0.883 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.29 - 1.65 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 0.981 - 1.18 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.84 - 2.20 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Vicat Softening Point | 204 °C | 399 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ N12 High Performance Polypropylene Nanocomposite
- Nilit RECONYL B KV30 Recycled nylon 6 for injection molding, 30% glass ball reinforced
- Lehmann & Voss LUVOCOM® 1850-8282 PBT, with carbon fiber
- SGL Carbon Group EK 10 Carbon Graphite
- SABIC Innovative Plastics LNP VERTON PV007 PA 6
- Solvay RHODASURF® LA 50 Surfactant
- Chem Polymer Chemlon 125 G Nylon 66, 25% Glass Sphere Reinforced
- Addiplast Addinyl A2 W Nylon 66
- BASF Sarcosine Sodium 40% Solution
- Overview of materials for Acetal Copolymer, Impact Modified
Copyright © lookpolymers.com All Rights Reserved