A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 0.50 - 1.5 g/10 min @Temperature 230 °C |
0.50 - 1.5 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ASTM D785 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Modulus | 2.207 GPa | 320.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Hexion Bakelite™ PF 38110 Phenolic Formaldehyde Resin, High Surface Quality (discontinued **)
- Huntsman HY 837 Aliphatic Amine
- Mearthane Durethaneâ„¢ S DS-450D Solid Polyurethane Elastomer
- Sylvin Technologies 9999-95 Natural PVC Molding Compound
- Techmer ES HiFill® ABS GF3 3% Glass Filled
- SMAC SMACWRAP® ST Damping Material, 0.60 mm
- TIMET TIMETAL® 5111 Titanium Alloy (Ti-5Al-1Sn-1Zr-1V-0.8Mo; ASTM Grade 32)
- Arkema Group Rilsan® AZM 50 NOIR T6LD Nylon 12, 50% Glass Fiber Filled (Dry)
- BASF Capron® HPN 9315G HS BK-102 Impact Modified, 15% Glass-Filled Nylon 6 (Conditioned) (discontinued **)<
Copyright © lookpolymers.com All Rights Reserved