Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ASTM D648 |
Nilit Polynil® P100 Medium Viscosity Nylon 66 Description: Polynil P100 is a grade has a viscosity that has been optimized for monofilament extrusion for high strength monofilaments.Key characteristics: Viscosity number 200 gr/cm3Excellent melt.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | DIN 53461; ASTM D648 |
Kolon KOPET® KP133G45 FR-PET Resin KOPET® is the FR-PET which realizes the good properties and surface of injection molding with good mold process of short cooling time in low molding temperature.Good mold release, good surface of.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
Gromax BFG30-B103N1 Nylon 6 33% Glass Filled (Conditioned) Information provided by Gromax Enterprises Corp. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
Gromax BFG30-B103N1 Nylon 6 33% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
Gromax BFG45-AS00N1 Nylon 6 46% Glass Filled (Conditioned) Information provided by Gromax Enterprises Corp. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
Gromax BFG45-AS00N1 Nylon 6 46% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
Gromax BFG45-B100N1 Nylon 6 46% Glass Filled (Conditioned) Information provided by Gromax Enterprises Corp. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
Gromax BFG45-B100N1 Nylon 6 46% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
Gromax BFG50-BN00N1 Nylon 6 60% Glass Filled (Conditioned) Information provided by Gromax Enterprises Corp. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
Gromax BFG50-BN00N1 Nylon 6 60% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP LUBRICOMP JX00061 PES (Europe-Africa-Middle East) LNP* Lubricomp* JX00061 is a compound based on Polyethersulfone resin containing Carbon Fiber, Proprietary Lubricant. Added features of this material include: Electrically Conductive. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 438 °F | ASTM D648 |
Solvay Technyl® A218 Heat Stabilized Nylon 66 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP Thermocomp OK006 PPS - Linear LNP* Thermocomp* OK006 is based on a Linear Polyphenylene Sulfide (PPS) containing Talc.This data was supplied by SABIC-IP for the Americas region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C @Thickness 3.20 mm |
439 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP VERTON RV00AE PA 66 LNP* VERTON* RV00AE is a compound based on Nylon 66 containing 50% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ASTM D648 |
Cheng Yu Plastic N6C2 Nylon 6, 20% Mineral Reinforced |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ASTM D648 |
Cheng Yu Plastic N6G15 Nylon 6, 15% Glass Filled |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ASTM D648 |
Cheng Yu Plastic T883GV25 Flame Retardant PBT, 25% Glass Fiber |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1/-2 |
DuPont Performance Polymers Sorona® 3030G BK001 Polytrimethylene Terephthalate (PTT)
(Unverified Data**)& 30% Glass Reinforced Polytrimethylene Terephthalate Sorona 3030G BK001 is a 30% glass reinforced black PTT resin containing 25% renewably sourced ingredients by weight (37% polymer basis) with good .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1/-2 |
DuPont Performance Polymers Sorona® 3030GV BK001 Polytrimethylene Terephthalate (PTT) 30% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Sorona 3030GV BK001 is a 30% glass reinforced black PTT resin containing 25% renewably sourced ingredients by weight (37% based .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ASTM D648 |
Ashley Polymers Ashlene® 525LD Nylon 66 High impact Nylon 66 with good stiffness, for injection molding.Data provided by the manufacturer |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ASTM D648 |
Ashley Polymers Ashlene® 539L Nylon 66 High viscosity for injection molding of heavy parts.Data provided by the manufacturer |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ASTM D648 |
Ashley Polymers Ashlene® 539 Nylon 66 Extrusion grade for film & monofilament.Data provided by the manufacturer |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ASTM D648 |
A. Schulman ComAlloy Lubrilon® 631 Nylon 6/6, Graphite/Molybdenum Disulfide Filled Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 - 255 °C | 439 - 491 °F | Average value: 245 °C Grade Count:14 |
Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 50% Glass Reinforced". Specific grades with glass content between 45% .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1/-2 |
DuPont Performance Polymers Sorona® 3030G BK001 Polytrimethylene Terephthalate (PTT)
(Unverified Data**)& Sorona® 3030G BK001 is a 30% glass reinforced black PTT resin containing 25% renewably sourced ingredients by weight (37% polymer basis) with good strength, stiffness and low warpage and superior s.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1/-2 |
DuPont Performance Polymers Sorona® 3030GV BK001 Polytrimethylene Terephthalate (PTT)
(Unverified Data**) Sorona® 3030GV BK001 is a 30% glass reinforced black PTT resin containing 25% renewably sourced ingredients by weight (37% based on polymer only) with low warpage and superior strength, stiffness a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1/-2 |
DuPont Performance Polymers Sorona® 3030GV NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data**) Sorona® 3030GV NC010 is a 30% glass reinforced PTT resin containing 25% renewably sourced ingredients by weight (37% based on polymer only) with low warpage and superior strength, stiffness and sur.. |