Gromax BFG45-AS00N1 Nylon 6 46% Glass Filled (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG45-AS00N1 Nylon 6 46% Glass Filled (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ISO 1183 |
| Moisture Absorption | 0.800 % | 0.800 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Pyrotek NAD-1000 High Temperature Engineering Board
- Overview of materials for Ethylene Vinyl Alcohol (EVOH)
- Lehmann & Voss LUVOCOM® 1800-8435 PET, with PTFE
- LG Chemical LUPOY GP2102 PC+GF10%
- Momentive Performance Materials TSE322B Black Adhesive Sealant, Non-Corrosive Flowable
- Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F)
- A. Schulman FORMION™ FI 395 Ionomer
- Ametek P303L P/M Stainless Steel, Sintered from 6.5 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved