Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 223 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	223 °C	433 °F	Annealed, 0.125 in bars; ASTM D648
PolyOne Lubri-Tech™ PS-30GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated (discontinued Description/Features:Glass Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Deflection Temperature at 0.46 MPa (66 psi)	223 °C	433 °F	ISO 75-1/-2
DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data** Sorona® FG3015G NC010 is a 15% glass fiber reinforced polytrimethylene terephthalate resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) formulated to be food c..
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C	433 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Europe-Africa-Middle East) LNP* Lubricomp* JFL36 is a compound based on Polyethersulfone resin containing Glass Fiber, PTFE.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C	433 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP RBG16I PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RBG16I is a compound based on Nylon 66 resin containing Glass Bead, Graphite. Added features of this material include: High Impact.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C	433 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP RBL36L PA 66 LNP* LUBRICOMP* RBL36L is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features s of this grade are: Low Extractable, Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C	433 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics ValoxÂ® SHF4340 PBT (Europe-Africa-Middle East) 20% GF Super High Flow PBT
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C @Thickness 3.20 mm	433 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics LNP Stat-kon WEF42 PET/PBT LNP Stat-Kon WCF-1006 is a compound based on PET/PBT resin containing carbon and glass fiber reinforcements.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C	433 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C	433 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP JF004RXP PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004RXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C	433 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP WC006 Polyester, TP (Asia Pacific) LNP* Thermocomp* WC006 is a compound based on Polyester, TP resin containing Carbon Fiber.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C @Thickness 6.40 mm	433 Â°F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics ValoxÂ® 430 PBT 33 % glass reinforced, impact modified. Connectors, etc.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C @Thickness 6.40 mm	433 Â°F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics ValoxÂ® 430 PBT (Asia Pacific) 33 % glass reinforced, impact modified. Connectors, etc.
Deflection Temperature at 0.46 MPa (66 psi)	223 Â°C	433 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT LNP* THERMOCOMP* WC006 is a compound based on PBT resin containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Deflection Temperature at 0.46 MPa (66 psi)	223 °C	433 °F	ASTM D648
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	223 °C	433 °F	ISO 75-1/-2
DuPont Performance Polymers Sorona® 3015GV NC010 Polytrimethylene Terephthalate (PTT) 15% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Sorona 3015GV NC010 is a 15% glass reinforced PTT resin containing 31% renewably sourced ingredients by weight (37% based on pol..
Deflection Temperature at 0.46 MPa (66 psi)	223 °C	433 °F	ASTM D648
A. Schulman ComAlloy Hiloy® 442 Glass Reinforced, PET Alloy Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi)	223 °C	433 °F	ISO 75-2
BASF Ultradur B 4406 G4 PBT Description: Is a PBT, flame-retardant injection-molding grades, with 20% glass fibers, for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and ligh..
Deflection Temperature at 0.46 MPa (66 psi)	223 °C @Thickness 6.40 mm	433 °F @Thickness 0.252 in	ASTM D648
Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR Information provided by Samsung Cheil Industries.
Deflection Temperature at 0.46 MPa (66 psi)	223 °C	433 °F	Unannealed; ASTM D648
LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant (discontinu Features: Heat Stabilized, Good Mold Release, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; ..