- PolyOne Lubri-Tech™ PS-30GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated (discontinued
PolyOne Lubri-Tech™ PS-30GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated (discontinued
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PS-30GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated
(discontinued.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 117 MPa | 17000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.40 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 217 °C | 423 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 271 °C | 470 - 520 °F | Molding |
| Mold Temperature | 65.6 - 107 °C | 150 - 225 °F | |
| Drying Temperature | 82.2 - 104 °C | 180 - 220 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Polyplastic Armlen® PP MF 20-3IM Impact Modified Polypropylene
- Magyar Aluminum ALO-EL-7P Alumina
- Michelman® Michem® Lube 368 Anionic paraffin/polyethylene wax emulsion
- KaMin Kamintex® Kaolin Clay - Calcined
- Solvay Specialty Polymers Cogegum® GFR/365 Polyolefin
- Master Bond EP21TDCHTND Versatile, toughened two component epoxy for bonding, sealing and coating
- COI Ceramics Sylramic™ S400 Silicon Carbide Ceramic Matrix Composite, Carbon
- Eurotec® Tecomid® NB40 NL RM PA 6 low friction and wear
- Ascend Performance Materials VYDYNE® R533 Nylon, 33% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved