LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant  (discontinu

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant  (discontinu.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Heat Stabilized, Good Mold Release, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
Method A; ASTM D792
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.10 %
0.10 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0080 cm/cm
0.0070 - 0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 192 MPa
27800 psi
ASTM D638
Tensile Strength, Yield 192 MPa
27800 psi
ASTM D638
Elongation at Break 3.5 %
3.5 %
ASTM D638
Elongation at Yield 3.5 %
3.5 %
ASTM D638
Tensile Modulus 11.9 GPa
1730 ksi
ASTM D638
Flexural Strength 276 MPa
40000 psi
ASTM D790
Flexural Modulus 9.03 GPa
1310 ksi
ASTM D790
Izod Impact, Notched 1.76 J/cm

@Thickness 3.18 mm
3.30 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 13.7 J/cm

@Thickness 3.18 mm
25.7 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 16.9 kJ/m²
8.04 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 88.3 kJ/m²
42.0 ft-lb/in²
ISO 180
Falling Dart Impact 11.8 J
8.70 ft-lb
ASTM D3763
Impact Test 4.76 J
3.51 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 223 °C
433 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 214 °C
417 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 268 - 274 °C
514 - 525 °F
Mold Temperature 82.2 - 93.3 °C
180 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.20 %
0.20 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi