- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 177 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 177 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | 120°C/h; ISO 75/1 |
| Polykemi AB SCANMID 6 B12^ NH6 Nylon 6, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| Polymer Resources NY6-GP1 General Purpose Nylon 6 General Purpose Nylon 6, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| Polymer Resources AC-G25 Acetal Copolymer, 25% Glass Reinforced Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | Unannealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® NJ-30GF/000 Nylon 12, Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 - 230 °C | 350 - 446 °F | Average value: 204 °C Grade Count:17 |
| Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 - 265 °C | 350 - 509 °F | Average value: 250 °C Grade Count:90 |
| Overview of materials for Nylon 66, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and ma.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 - 204 °C | 351 - 400 °F | Average value: 197 °C Grade Count:7 |
| Overview of materials for Nylon 612, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Aramid Fiber Filled". Each property range of values reported is minimum and maximum values of.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 |
| PolyOne Lubri-Tech™ NL-15KV/05M Nylon 6/12 - 15% Kevlar Fiber - 5% MoS2
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp GL004 PSU (Asia Pacific) LNP* Lubricomp* GL004 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp GL004 PSU (Asia Pacific) LNP* Lubricomp* GL004 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM L N Availability: North AmericaForms: PelletsAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedAppearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM L W N Availability: North AmericaForms: PelletsAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedAppearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP SCL36 PA12 LNP* LUBRICOMP* SCL36 is a compound based on Nylon 12 resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12 LNP* LUBRICOMP* SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_NC2525 PPE+PS LNP* Stat-kon* Noryl_NC2525 compound is a 25% CFR PPE+PS. Highly conductive. High heat. May be added to similar material/regrind to add some conductivity to the blend. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON SE003 PA 12 (Europe-Africa-Middle East) LNP* Stat-kon* SE003 is a compound based on Nylon 12 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 |
| Adell BI-10 Nylon 6, Impact Modified Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 |
| Ashley Polymers Ashlene® 735LD Nylon 6 An impact modified, plasticized copolymer with improved impact resistance for injection molding.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| Aaron Industries AAROPRENE® AEN 6000-2 Nylon 6 Engineered Resin |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 |
| ALM PA 606-FR Filled Nylon 12 Prototyping Polymer Only commercially available fire retardant nylon 12 material, which meets FAR 25.853 60 second burn specification.The parts produced from PA 606-FR have a much smoother surface finish and sharper fe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 |
| PolyOne Lubri-Tech™ SF-000/40T Polyphenylene Sulfide - 40% PTFE
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 |
| Adell AI-30 Nylon 66, Impact Modified Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® SF-10GF/000 Polyphenylene Sulfide (PPS), Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | DIN 53461 |
| Polyram PlusTek RA320G3 Nylon 6.6, 15% Glass Fiber, Flame Retardant 15% glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||