- Polyram PlusTek RA320G3 Nylon 6.6, 15% Glass Fiber, Flame Retardant
Polyram PlusTek RA320G3 Nylon 6.6, 15% Glass Fiber, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA320G3 Nylon 6.6, 15% Glass Fiber, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | DIN 53479 |
| Water Absorption | 7.0 % | 7.0 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0035 - 0.0045 cm/cm | 0.0035 - 0.0045 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM-D785 |
| Tensile Strength, Yield | 105 MPa | 15200 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous Use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 41 UVT General Purpose Acrylic Resin
- Pau Tai UNISTAB CZ-80 Non-toxic Calcium-Zinc Stabilizer
- Kazanorgsintez 153-15 Composition of Low Density Polyethylene, Crack-Proof
- LTL Color Compounds ColorFast® PBT100 PBT
- Sharadaa Ceramics Sharada RFC-LW Gel Bonded Castables
- SABIC Innovative Plastics LNP THERMOCOMP OF006A PPS (Europe-Africa-Middle East)
- Zeon Chemicals Hydrin® T3105 Polyepichlorohydrin Elastomer
- Arlon 19646B025 Silicone Rubber/Fiberglass Laminate
- Resinoid 1322 Phenolic Molding, Glass Reinforced
- BASF 2-Phenylethylamine
Copyright © lookpolymers.com All Rights Reserved