PolyOne Edgetek® SF-10GF/000 Polyphenylene Sulfide (PPS), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® SF-10GF/000 Polyphenylene Sulfide (PPS), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.406 g/cc | 1.406 g/cc | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0055 cm/cm | 0.0050 - 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 5.52 GPa | 800 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | Molding |
| Mold Temperature | >= 135 °C | >= 275 °F | |
| Drying Temperature | 135 °C | 275 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB FS-320 Foam Stabilizer
- SABIC Innovative Plastics Cycoloy® C1110HF PC+ABS (Asia Pacific)
- Kazanorgsintez Polyethyleneglycol-35, Refined
- Taiwan Sheen Soon Sheenthane® A9600R Thermoplastic Polyurethane Elastomer
- Sharadaa Ceramics ZAP 012 Smart Cast Application
- Daikin DAI-EL G-752 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
- Aclo Accutech Polypropylene Homopolymer HP0339T20L Talc Reinforced
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with Control Plasticizer
Copyright © lookpolymers.com All Rights Reserved