- PolyOne Lubri-Tech™ NL-15KV/05M Nylon 6/12 - 15% Kevlar Fiber - 5% MoS2 (discontinued **)
PolyOne Lubri-Tech™ NL-15KV/05M Nylon 6/12 - 15% Kevlar Fiber - 5% MoS2 (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Aramid Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ NL-15KV/05M Nylon 6/12 - 15% Kevlar Fiber - 5% MoS2
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm @Thickness 3.17 mm |
0.010 - 0.020 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 2.0 - 5.0 % | 2.0 - 5.0 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 - 0.640 J/cm @Thickness 6.35 mm |
0.806 - 1.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Stock |
| Mold Temperature | 93.0 - 107 °C | 199 - 225 °F | |
| Drying Temperature | 93.0 - 107 °C | 199 - 225 °F |
Users viewing this material also viewed the following:
- MV Labs HG800 HgO Mercury(II) oxide
- Polymax® Maxelast® F02-081A-10C TPE, Halogen Free Extrusion Grade
- Lord Adhesives Thermosetâ„¢ ME-430 Epoxy Board Level Encapsulant
- Gwent Electronic Materials C2050425D1 Curable Carbon Ink
- Lucite International Lucite® 30B Acrylic Bead Resin
- Polyram RamLloy PZF301G4 PC/PBT Alloy, 20% Glass Fiber
- Universal Wire Works ER309L Stainless Steel Bare Wire
- A. Schulman POLYBATCH™ Green 3315 Concentrate Based In Polyethylene
- Arlon 920-07Rxx-P0 0.020" (0.508 mm) Self-Fusing Silicone Tape
- Arlon Thermavac® 0.060" (1.524 mm) Cured Silicone Vacuum Bagging (10502N060)
Copyright © lookpolymers.com All Rights Reserved