- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 124 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 124 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Multibase Multi-Pro® 3018 TU Polypropylene Talc Filled, 30% by weight.Forms:PelletsProcessing Methods:Injection MoldingUses: Automotive Under the HoodInformation provided by Multibase |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CPQ10015 FF Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Polymer Resources PC-IM2 Polycarbonate, Impact Modified, Medium Flow Polycarbonate, Impact Modified, Medium FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| RheTech Products M25P100-01 25% Mica Reinforced Polypropylene, Black Applications: Underhood applicationsInternal I/P ComponentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Lexan® EXRL0683 PC Copolymer 11 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1433 PC Copolymer (Asia Pacific) 11 MFR LEXAN High Flow Ductile Copolymer UV stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1910 PC Copolymer (Europe-Africa-Middle East) 55 MFR LEXAN High Flow Ductile Copolymer, Natural colors only |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 - 138 °C | 255 - 280 °F | Average value: 130 °C Grade Count:5 |
| Overview of materials for Polycarbonate/Styrenic Alloy This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Styrenic Alloy". Each property range of values reported is minimum and maximum values of a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 6.40 mm |
255 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa MAC-601 DY Modified 60/40 PC/ABS Alloy Features:Excellent balance propertiesHigh impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile instrument panelPower toolComputer and acce.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 CM40 6122 BK 40% Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 40% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedAppearance: BlackProcessing Method: Injection Mol.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Europe-Africa-Middle East) PC-Siloxane copolymer + Polyester alloy, High Impact, Transparent |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xylex X7503HP PC+POLYESTER (Europe-Africa-Middle East) Clear PC-Siloxane copolymer + Polyester alloy, USA Food ContactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-LOY KX05015 Acetal Copolymer (Europe-Africa-Middle East) LNP* Stat-Loy* KX05015 is a compound based on Acetal Copolymer resin containing Antistat. Added features include permanent Anti-Static. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® X5601WX PBT + PC + PET Impact modified PBT+PC+PET, Heat aging improved Xenoy |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Styron PULSEâ„¢ 2300 PT PC/ABS Engineering Resin Information provided by Styron |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL BN9003G PPE+HIPS PPE+PS blend. Unfilled. Blow molding. Excellent balance of impact and surface aesthetics. Suitable for automotive exterior components including spoilers. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL EM6100 PPE+PS PPE+PS blend. Unfilled. Good balance of flow/heat/impact. Dimensional stability. Paint adhesion. Suitable for the automotive interior market: HVAC housings, radio components. MS-DB424, WSB-M4D844-A9.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1285H is a 20% glass reinforced copolymer polypropylene compound. It has good impact and heat resistance. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200H is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1285H is a 20% glass reinforced copolymer polypropylene compound. It has good impact and heat resistance. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Clariant Renol PCSP0007 Polycarbonate/Polyester Alloy Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Clariant Renol PCSP0016BL-201 Polycarbonate/Polyester Alloy Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Aaron Industries AAROPRENE® TFPP 2020 Talc Filled Polypropylene AAROPRENE® TFPP 2000 Series Talc Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Adell EA-16 Homopolymer Polypropylene, 30% Talc Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Asahi Kasei Thermofil P6-30MI-0533 30% Mica Reinforced, Flame Retardant, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Ashley Polymers Ashlene® 1105 Polycarbonate, 5-7% Glass Reinforced A general purpose foamable injection molding grade resin with 5-7% glass reinforcement.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Aaron Industries AAROPRENE® TFIPP 2040 High Impact Talc Filled Polypropylene AAROPRENE® TFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Multibase Multi-Flam™ 0102 Natural PP Polypropylene Features:Flame Retardant Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200H is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | |
| Polimeri Europa KOBLEND PCA 638F PC+ABS
(discontinued **) Symbol according to ISO 1043/1: PC+ABS Similar to KOBLEND PCA 638 with an improved fluidity, suitable to mould complex items. Unfilled. Suitable for Injection Molding. Supplied as pellets.ISO dat.. |
|||