- SABIC Innovative Plastics Xenoy® X5601WX PBT + PC + PET
SABIC Innovative Plastics Xenoy® X5601WX PBT + PC + PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PET + PBT Unreinforced , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X5601WX PBT + PC + PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified PBT+PC+PET, Heat aging improved Xenoy
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.20 mm |
0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 14 g/10 min @Load 5.00 kg, Temperature 266 °C |
14 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 265 °C |
14 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | 50 mm/min; ISO 527 |
| 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 93 % | 93 % | Type I, 50 mm/min; ASTM D638 |
| 118 % | 118 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.28 GPa | 331 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 8.17 J/cm | 15.3 ft-lb/in | ASTM D256 |
| 2.47 J/cm @Temperature -30.0 °C |
4.63 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 62.0 kJ/m² | 29.5 ft-lb/in² | 80*10*4; ISO 180/1A |
| 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Dart Drop, Total Energy | 55.0 J @Temperature 23.0 °C |
40.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 71.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 71.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 101 °C @Thickness 3.20 mm |
214 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ISO 306 |
| 131 °C | 268 °F | Rate B/50; ASTM D1525 | |
| 132 °C | 270 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Plansee WRe5 Tungsten-Rhenium Alloy
- Rogers Corporation Ultralam® 3908 Liquid Crystalline Polymer Circuit Material
- Cookson Group Plaskon® 440S Mineral Filled Novolac Epoxy Molding Compound (discontinued **)
- Huntsman MY 0500 Multifunctional Resin
- Lucas-Milhaupt BRAZE 560
- Borealis Borclean™ HB300BF Polypropylene Homopolymer for Capacitor Film
- Arkema Group Evatane® 1090 VN 3 Ethylene Vinyl Acetate
- 3M Dyneon™ PVDF 32008/0000 Polyvinylidene Fluoride (discontinued **)
- Overview of materials for ABS/PVC Alloy
Copyright © lookpolymers.com All Rights Reserved