SABIC Innovative Plastics NORYL BN9003G PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL BN9003G PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. Unfilled. Blow molding. Excellent balance of impact and surface aesthetics. Suitable for automotive exterior components including spoilers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0055 - 0.0075 cm/cm | 0.0055 - 0.0075 in/in | on Tensile Bar; SABIC Method |
| 0.0055 - 0.0075 cm/cm @Thickness 3.20 mm |
0.0055 - 0.0075 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0055 - 0.0075 cm/cm @Thickness 3.20 mm |
0.0055 - 0.0075 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 280 °C |
10 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 12 g/10 min @Load 5.00 kg, Temperature 280 °C |
12 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 |
| 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 30.4 % | 30.4 % | 50 mm/min; ISO 527 |
| 45 % | 45 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 3.4 % | 3.4 % | 50 mm/min; ISO 527 |
| 3.6 % | 3.6 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.17 GPa | 315 ksi | 1 mm/min; ISO 527 |
| 2.24 GPa | 325 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.15 GPa | 312 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.19 GPa | 318 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D256 |
| 1.27 J/cm @Temperature -30.0 °C |
2.38 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| 54.0 kJ/m² @Temperature -30.0 °C |
25.7 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 10.7 J/cm² @Temperature -30.0 °C |
50.9 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 2.60 J/cm² | 12.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 40.0 J @Temperature 23.0 °C |
29.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 86.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 86.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 127 °C | 261 °F | Rate B/50; ISO 306 |
| 130 °C | 266 °F | Rate B/120; ISO 306 | |
| 141 °C | 286 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE4472L PC (Asia Pacific)
- PolyOne Geon™ Vinyl Wire & Cable WR7400L Polyvinyl Chloride, Flexible (PVC, Flexible)
- ExxonMobil Escorene® LD-317 EVA Film Resin, FMI (discontinued **)
- Huntsman Araldite GT 7014 Bisphenol A Epoxy Solid Resin
- Mateck GaSb
- Techmer ES Plaslube® J-1/CF/15/TF/20 NAT PA66
- Borealis Borflow™ HL508FB Polypropylene Homopolymer
- Lubrizol Stat-Rite® M-690 Static Control PETG Alloy
- Unifrax Fiberfrax® Washed 757 High Purity High-Index Fiber
- Esstech X-887-7446 1,6-Hexanediol Dimethacrylate, C14H22O4
Copyright © lookpolymers.com All Rights Reserved