SABIC Innovative Plastics Xylex X7503HP PC+POLYESTER (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xylex X7503HP PC+POLYESTER (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clear PC-Siloxane copolymer + Polyester alloy, USA Food ContactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %

@Temperature 23.0 °C
 0.50 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 8.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D 1238
8.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 8.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.0 MPa
7830 psi
50 mm/min; ISO 527
55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D 638
58.0 MPa
8410 psi
50 mm/min; ISO 527
Elongation at Break 100 %
100 %
Type I, 50 mm/min; ASTM D 638
100 %
100 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D 638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D 638
2.10 GPa
305 ksi
1 mm/min; ISO 527
Flexural Yield Strength 84.0 MPa
12200 psi
2 mm/min; ISO 178
86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 1.90 GPa
276 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.10 GPa
305 ksi
2 mm/min; ISO 178
Izod Impact, Notched 7.50 J/cm

@Temperature -30.0 °C
 14.1 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
9.20 J/cm

@Temperature 23.0 °C
 17.2 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 17.0 kJ/m²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
68.0 kJ/m²

@Temperature 23.0 °C
 32.4 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 7.00 J/cm²

@Temperature 23.0 °C
 33.3 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 71.0 J

@Temperature 23.0 °C
 52.4 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
77.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 42.8 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
78.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 43.3 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 124 °C
255 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
124 °C

@Thickness 3.20 mm
 255 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
110 °C

@Thickness 3.20 mm
 230 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 130 °C
266 °F
Rate B/50; ISO 306
132 °C
270 °F
Rate B/120; ISO 306
132 °C
270 °F
Rate B/50; ASTM D 1525
Optical Properties Metric English Comments
Haze 2.0 %

@Thickness 2.54 mm
 2.0 %

@Thickness 0.100 in
 ASTM D 1003
Transmission, Visible 86 %

@Thickness 2.54 mm
 86 %

@Thickness 0.100 in
 ASTM D 1003