- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 118 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 118 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648-95 |
| Multibase Multi-Pro® 4006 T H BLK 40% Talc Content Polypropylene Multi-Pro 4002 T H is a talc reinforced polypropylene compound with excellent stiffness at medium impact resistance. Its heat resistance is improved over natural and can resist 150°C for 750 hours.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.18 mm |
244 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ PPC-30T UV EXT 1148 Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.18 mm |
244 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ STFPP.1220 BK-L Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| RheTech Products M40P200-01 40% Mica Reinforced Polypropylene Copolymer, Black Applications: Automotive applicationsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| RheTech Products T10P100-00 10% Talc Reinforced Polypropylene, Natural Applications: Consumer goodsIP structural componentsInterior trimInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| RheTech Products T10P100-01 10% Talc Reinforced Polypropylene, Black Applications: Consumer goodsAir ductsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| RheTech Products T40P250-00 40% Talc Reinforced Polypropylene Copolymer, Natural Applications: BracketsHousingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| SABIC PP 518A Polypropylene Homopolymer for Fiber Applications Product Description: PP 518A is a PP homopolymer with a broad molecular weight distribution intended for fiber extrusion applications.PP 518A has the following features:Consistent processabilityGoo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CS9610 PC+ABS Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CS9610 PC+ABS (Europe-Africa-Middle East) Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CS9610 PC+ABS (Asia Pacific) Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T15020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| BP Amoco Acctuf® 3119HS Ultra High Impact Copolymer Polypropylene
(discontinued **) Suggested fabrication methods: Extrusion; ThermoformingFeatures: High stiffness, Low Temperature impactComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from inject.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-1120 AN 20% Talc-Filled Polypropylene Homopolymer INNOPOL® CS 1-1120 AN is a 20% talc-filled polypropylene homopolymer compound /PP-H TD20 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 1-1120 AN is develo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON FX98501 PE LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PC/PBT IM 1799 BK Availability: North AmericaForms: PelletsAdditive: Impact ModifierFeatures: Impact ModifiedAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PC/PBT IM 6600 Availability: North AmericaForms: PelletsAdditive: Impact ModifierFeatures: Impact ModifiedAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PP GB40 40% Glass Beads Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 40% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-2 |
| Borealis Bormod™ HC905TF Polypropylene Homopolymer for Thermoforming Bormod HC905TF is a low melt flow rate polypropylene homopolymer intended for thermoformed packaging applications. This homopolymer is produced using the Borealis Controlled Crystallinity Polypropy.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1666 is a 10% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1666 is a 10% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-1/-2 |
| Covestro Bayblend® KU 1-1446* Polycarbonate + ABS Developmental productGrade with improved low-temperature impact strength and petrol resistance for automotive partsin version BBS904 suitable for extrusion/extrusion blow molding and electroplating .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336M30L Mica Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1200 is a 40% calcium carbonate-filled homopolymer polypropylene. Information provided by A. Schulman. |
|||