Techmer ES Plastiblend® PC/PBT IM 6600
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Techmer ES |
| Trade Name | Plastiblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plastiblend® PC/PBT IM 6600.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Impact ModifierFeatures: Impact ModifiedAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 3.17 mm |
0.0080 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Flexural Yield Strength | 84.1 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 7.47 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
14.0 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 7.47 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
14.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 82.8 µm/m-°C | 46.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- Karina E900D10/1-E-IS-BZ White PVC Compound
- Shakespeare FL-8 Fluorocarbon PVDF Fishing Line, 20 lb
- Styrolution Luran® 388 S SAN
- Domo 2300L Polypropylene Copolymer
- EMS-Griltech Grilene® KE 170 CoPES Mono-Component Fusible Adhesive Fiber
- 3M Scotch® 8886 Stretchable Tape
- A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene
- Zircar Zirconia ZR-CEM Zirconia Cement
- HP Alloys Alloy X, 15% Cold Worked
Copyright © lookpolymers.com All Rights Reserved