Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
SABIC Innovative Plastics Cycoloy® CM4219 PC+ABS (Asia Pacific) |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature 23.0 - 100 °C |
21.1 µin/in-°F @Temperature 73.4 - 212 °F |
|
Manifattura Cattaneo VESPEL® SP22 Polyimide Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP LUBRICOMP REL22 PA 66 LNP* LUBRICOMP* REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 LNP LUBRILOY* RF206 is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material includes: Wear Resistant. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP LUBRILOY RF206AXH PA 66 LNP LUBRILOY* RF206AXH is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material include: Wear Resistant, Healthcare. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
SABIC Innovative Plastics LNP STAT-KON EEF42 PEI LNP STAT-KON* EEF42 is a compound based on Polyetherimide resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
21.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOCOMP JF002 PES (Europe-Africa-Middle East) LNP* Thermocomp* JF002 is a compound based on Polyethersulfone resin containing Glass Fiber. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
Styron CALIBREâ„¢ 5101-15 Polycarbonate Resin Overview: CALIBREâ„¢ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding .. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
21.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOTUF VF004S SUPER TOUGH NYLON (Europe-Africa-Middle East) LNP* THERMOTUF* VF004S is a compound based on Super Tough Nylon resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | ISO 11359-1/-2 |
Covestro Bayblend® T88 GF-10* Polycarbonate + SAN Glass Filled Impact Grade Developmental productInjection molding grade10 % GFoptimized heat ageing- and UV-stabilityvery good flowtensile modulus = 5100 MPaVicat/B 120 = 134 °CPreprocessingMax. Water content |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature 20.0 °C |
21.1 µin/in-°F @Temperature 68.0 °F |
|
Covestro Makrolon® 9415(Z) Polycarbonate Medium viscosity, flame retardant extrusion and injection molding grade with 10% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer Materia.. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | ISO 11359 |
BASF Ultramid® B3GM35 Q611 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid B3GM35 Q611 is a 40% combined glass-fiber and mineral reinforced injection molding PA6 grade. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | ASTM E831 |
Proto3000 PC Fused Deposition Modeling Polymer Description: A true industrial thermoplastic, PC (polycarbonate) is widely used in automotive, aerospace, medical and many other applications. PC offers accuracy, durability and stability, creating .. |
|||
CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP THERMOCOMP RF007SXN PA 66 LNP* THERMOCOMP* RF007SXN is a Hydro-Stable, 35% Glass Fiber reinforced compound based on Nylon 66. Added features of this grade include: Heat Stabilized, NSF Listed. |