SABIC Innovative Plastics LNP LUBRILOY RF206AXH PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY RF206AXH PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* RF206AXH is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material include: Wear Resistant, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.380 % | 0.380 % | 50% RH, 24 hrs; ASTM D570 |
| 0.660 % | 0.660 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 118 MPa | 17100 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.46 GPa | 1230 ksi | 1 mm/min; ISO 527 |
| 8.76 GPa | 1270 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 167 MPa | 24200 psi | ISO 178 |
| 173 MPa | 25100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.06 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.14 J/cm | 2.14 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.90 J/cm | 12.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.40 | 0.40 | ASTM D3702 Modified |
| K (wear) Factor | 90.6 x 10-8 mm³/N-M | 45.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 241 °C @Thickness 3.20 mm |
466 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Pyrotek MT-29Q Quilted Microporous Insulation
- Karina 813D11/4-IS-AS Bronze PVC Compound
- Lehmann & Voss LUVOCOM® 1105-7023/GY PEEK, with glass fiber
- Sumitomo Bakelite North America RX® 613 Fiberglass Reinforced Phenolic
- DuPont Performance Polymers Crastin® SK608 BK509 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Diamond Polymers NPP25-0303 GF20 20% Glass Filled Polypropylene
- DuPont Teijin Films Mylar® P25 Polyester Film, 75 Gauge
- ChevronTexaco NLGI 2 SRI Grease
- Fainplast Compounds CKL 173 Flexible PVC, Sheathing Lead Free
- Braskem MR 435 UV LMDPE Rotational Molding Polyethylene
Copyright © lookpolymers.com All Rights Reserved