SABIC Innovative Plastics Cycoloy® CM4219 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® CM4219 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 260 °C |
18 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 94.0 MPa | 13600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.80 GPa | 841 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.93 GPa | 715 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*3; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
UL 94 |
Users viewing this material also viewed the following:
- ExxonMobil Santoprene® 221-55 Thermoplastic Elastomer (discontinued **)
- Chevron Phillips Ryton® PR25 Polyphenylene Sulfide Resin (discontinued **)
- Huntsman IROGRAN® A 85 H 4827 TPU-Polyester
- SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS
- Shandong Dongyue Polymer DF-16 PTFE Molding Powder (Micronized Particles)
- Schmolz + Bickenbach Thermodur® 2714 Extra Fine Structure - Hot Work Die Steel
- Total HL 428 HDPE film resin
- CP-Polymer-Technik Wellamid® 6600 MR 209 HWCP 20% Mineral Nylon 66, Heat Stabilized, Dry
- EVALCA EVAL® EF-XL Ethylene Vinyl Alcohol Copolymer Film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved