Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 114 °C | 237 °F | 10 N - 120°C/h; ISO 306/A120 |
Polimeri Europa Sinkral® C 442 ABS Resin Sinkral C 442 is a heat resistant injection molding grade offering good flow and impact resistance together with excellent thermal stability during processing. Designation: Thermoplastic ISO 2580-AB.. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/120; ISO 306 |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Asia Pacific) Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/120; ISO 306 |
SABIC Innovative Plastics Lexan® BPL1000 PC (Europe-Africa-Middle East) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U.. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/120; ISO 306 |
SABIC Innovative Plastics Lexan® ML7677 PC (Asia Pacific) Transparent Polycarbonate in limited colors. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ASTM D1525 |
SABIC Innovative Plastics Lexan® ML7677 PC (Asia Pacific) Transparent Polycarbonate in limited colors. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/120; ISO 306 |
SABIC Innovative Plastics Lexan® ML7677A PC (Asia Pacific) Commercial grade for Polycarbonate in only nature color. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm.This data was supplied by SABIC-IP for the Asia Pacific reg.. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ASTM D 1525 |
SABIC Innovative Plastics Lexan® ML7677A PC (Asia Pacific) Commercial grade for Polycarbonate in only nature color. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm.This data was supplied by SABIC-IP for the Asia Pacific reg.. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/120; ISO 306 |
SABIC Innovative Plastics Lexan® ML7686 PC (Asia Pacific) Transparent Polycarbonate in limited colors. Excellent processability, super high flow. UL rated V-2 at 1.5mm. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ASTM D1525 |
SABIC Innovative Plastics Lexan® FST3403 PC Copolymer Lexan* FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior .. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ISO 306 |
SABIC Innovative Plastics Lexan® FST3403 PC Copolymer Lexan* FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior .. |
|||
Vicat Softening Point | 114 °C | 237 °F | ISO 306 |
Total Lacqtene® 2006 PBK 35 HDPE pipe, sheet
(discontinued **) LACQTENE® 2006 PBK 35 is a medium density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2006 PBK 35 may be used for pipe extrusion (micro-irriga.. |
|||
Vicat Softening Point | 114 °C @Load 5.00 kg |
237 °F @Load 11.0 lb |
50°C/h; ASTM D1525 |
LG Chemical XR409H ABS, Heat Resistance Feature: Injection Molding, Heat ResistanceApplication: Automotives Interior Housing (Switch Panel Housing etc)CAS No. 25120-20-1, 9003-56-9, 25747-74-7, and 31621-07-5Information provided by LG Ch.. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ISO 306 |
SABIC Innovative Plastics NORYL WCV072 PPE+PP (Asia Pacific) Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De.. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ASTM D1525 |
SABIC Innovative Plastics NORYL WCV072 PPE+PP (Europe-Africa-Middle East) Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De.. |
|||
Vicat Softening Point | 114 °C | 237 °F | 50°C/hr, 50N; ISO 306 |
Teijin Multilon T-3713 Standard PC/ABS Polymer Alloy General grade of PC/ABS polymer alloy, having improved impact strength and heat resistance compared with a heat resistant ABS and flame retardant m-PPE and also having higher flowability compared wi.. |
|||
Vicat Softening Point | 114 °C | 237 °F | B/120; ISO R306 |
Samsung Cheil Industries Infino® NH-1037 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Vicat Softening Point | 114 °C @Load 1.02 kg |
237 °F @Load 2.25 lb |
Rate B (120°C/h); ASTM D1525 |
Styron XU 73120.00 Polycarbonate Resin Overview: XU 73120.00 Experimental Polycarbonate Resin is a high flow ignition resistant PC blend that contains no chlorinated or brominated additives. This resin is specifically designed to offer e.. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ISO 306 |
SABIC Innovative Plastics Noryl NH3060 PPE+HIPS NH3060 resin is a modified PPE + PS blend with an excellent balance of non-chlorinated non-brominated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific .. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/120; ISO 306 |
SABIC Innovative Plastics Noryl PX0003 PPE+HIPS PX0003 resin is a modified PPE+PS blend with an excellent balance of non-chlorinated non-brominated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific gr.. |
|||
Vicat Softening Point | 114 °C | 237 °F | 10 N; ISO 306 |
Borealis Borseal™ TD110BF Terpolymer for BOPP Film Borseal TD110BF is a C2/C4 terapolymer film resin.Borseal TD110BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Vicat Softening Point | 114 °C | 237 °F | 10 N; ISO 306 |
Borealis Borseal™ TD115BF Terpolymer for BOPP Film Borseal TD115BF is a C2/C4 terapolymer film resin.Borseal TD115BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Vicat Softening Point | 114 °C | 237 °F | 10 N; ISO 306A |
Borealis Borseal™ TD215BF Terpolymer for BOPP Film Borseal TD215BF is a C2/C4 terapolymer film resin.Borseal TD215BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Vicat Softening Point | 114 °C | 237 °F | 10 N; ISO 306A |
Borealis Borseal™ TD218BF Terpolymer for BOPP Film Borseal TD218BF is a C2/C4 terapolymer film resin.Borseal TD218BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Vicat Softening Point | 114 °C | 237 °F | ISO 306 |
Unipetrol PE HD LITEN® SB/SL 20 HDPE Made for blow molding, tubular film and special applications.Information provided by Unipetrol RPA |
|||
Vicat Softening Point | 114 °C | 237 °F | ASTM D1525 |
Westlake MC3016 High Density Polyethylene Coating Westlake MC3016 is a high density polyethylene designed for extrusion coating and lamination applications. MC3016 provides improved barrier properties, temperature resistance, stress crack resistanc.. |
|||
Vicat Softening Point | 114 °C | 237 °F | ExxonMobil Method |
ExxonMobil Pax-Plus™ 3204 Blown Film Resin Pax-Plus 3204 is a rubber modified high density polyethylene film resin which is used primarily in film requiring good impact strength. It is specially formulated to provide easy tear in the machin.. |
|||
Vicat Softening Point | 114 °C | 237 °F | |
Covestro Bayblend® KL 1-1430 Polycarbonate/ABS Blend Standard grade for cars.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ISO 306 |
SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Asia Pacific) CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of properties |
|||
Vicat Softening Point | 114 °C | 237 °F | 50°C/hr; 50N |
Arkema Group Pebax® MX 1205 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 40 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness.. |