SABIC Innovative Plastics NORYL WCV072 PPE+PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCV072 PPE+PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. Designed for evaluation in applications requiring ISO6722. 72 Shore D hardness. Processed using standard extrusion equipment.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.12 % | 0.12 % | ISO 62 |
| Melt Flow | 13.8 g/10 min @Load 5.00 kg, Temperature 280 °C |
13.8 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 13 g/10 min @Load 5.00 kg, Temperature 280 °C |
13 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | Type I, 50 mm/min; ASTM D638 |
| 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 46 % | 46 % | 50 mm/min; ISO 527 |
| 83 % | 83 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 11 % | 11 % | 50 mm/min; ISO 527 |
| 15 % | 15 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.71 GPa | 248 ksi | 50 mm/min; ASTM D638 |
| 1.75 GPa | 254 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 53.0 MPa | 7690 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 59.0 MPa | 8560 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.55 GPa | 225 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.74 GPa | 252 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.09 J/cm | 5.79 ft-lb/in | ASTM D256 |
| 0.670 J/cm @Temperature -30.0 °C |
1.26 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 3.30 J/cm² | 15.7 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 45.0 J @Temperature 23.0 °C |
33.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 85.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 111 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 114 °C | 237 °F | Rate B/50; ASTM D1525 |
| 114 °C | 237 °F | Rate B/50; ISO 306 | |
| 117 °C | 243 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID/L: 10-20/5-10 nm/0.5-2 um Short Multi-Walled Carbon Nanotubes
- Pasargad Polymer Peyvand Pasalac 3P-H6000B ABS
- Hexion Bakelite™ PF 2774 Phenolic Formaldehyde Resin, Dishwasher Proof, Improved Electrical Properties, Low Shrinkage, UL Listed
- I. Stern WC-102 General Purpose Crystal Polystyrene
- Less Common Metals SmCo5 Samarium Cobalt Alloy; Vacuum Induction Melting & Casting
- Styrolution PS 168 N/L GPPS
- Unipetrol PP MONSTEN® GH 001 Polypropylene Homopolymer
- Fainplast Compounds FK 91 Flexible PVC, Insulation Lead Free
- DuPont Elvax® 3175LG Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion (discontinued **)
Copyright © lookpolymers.com All Rights Reserved