Teijin Multilon T-3713 Standard PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon T-3713 Standard PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General grade of PC/ABS polymer alloy, having improved impact strength and heat resistance compared with a heat resistant ABS and flame retardant m-PPE and also having higher flowability compared with a heat resistant ABS.Applications:Mechanical components. Electric and electronic components, Safety and industrial equipment components.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Thickness 4.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 4.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50mm/min; ISO 527 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50mm/min; ISO 527 |
| Elongation at Break | 120 % | 120 % | 50mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
| Vicat Softening Point | 114 °C | 237 °F | 50°C/hr, 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Nye Lubricants 200A (SO) Synthetic Oil
- Sibur MPP 23007-E10 Frost Resistant Polypropylene
- A. Schulman PAPERMATCH® T-39617 Specialty Masterbatch
- ChevronTexaco Gear Compounds EP, ISO 460
- EMS-Griltech Griltex® D 1377E Copolyester Hotmelt Adhesive (Technical Applications)
- Esstech V-117-1112 Barium Borosilicate Glass
- DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 75 Gauge
- ConocoPhillips El Mar® 3000 Oil SAE Grade 40
- 3M Scotch-Weld™ TL77 Threadlocker Anaerobic Adhesive
Copyright © lookpolymers.com All Rights Reserved