SABIC Innovative Plastics Noryl PX0003 PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl PX0003 PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PX0003 resin is a modified PPE+PS blend with an excellent balance of non-chlorinated non-brominated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific gravity for light-weight parts. This injection molding resin is available in custom colors and meets UL 94 V-0 requirements at 1.5 mm. PX0003 may be an excellent candidate for industrial battery applications.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D 792 |
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.090 % | 0.090 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.11 % @Temperature 23.0 °C |
0.11 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0034 - 0.0052 cm/cm @Thickness 3.20 mm |
0.0034 - 0.0052 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 36 g/10 min @Load 5.00 kg, Temperature 280 °C |
36 g/10 min @Load 11.0 lb, Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 42 g/10 min @Load 5.00 kg, Temperature 280 °C |
42 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D 638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 8.0 % | 8.0 % | Type I, 50 mm/min; ASTM D 638 |
| 8.0 % | 8.0 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D 638 |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.75 GPa | 399 ksi | 5 mm/min; ASTM D 638 |
| 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
| 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.70 GPa | 392 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.70 GPa | 392 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm @Temperature -30.0 °C |
1.59 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 1.20 J/cm @Temperature 23.0 °C |
2.25 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 40.0 J @Temperature 23.0 °C |
29.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 84.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 112 °C | 234 °F | Rate B/50; ASTM D 1525 |
| 112 °C | 234 °F | Rate B/50; ISO 306 | |
| 114 °C | 237 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.3 @Frequency 1.00e+6 Hz |
2.3 @Frequency 1.00e+6 Hz |
ASTM D 150 |
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
ASTM D 150 |
Users viewing this material also viewed the following:
- Polymer Resources ABS-FR1 ABS, Flame Retardant
- Plastcom SLOVALEN PH 59 T 40 LW 031 PP, 40% mineral filling, laser label
- Total Lacqtene® 2001 TMA 46 HDPE pipe (discontinued **)
- Sibur 23007-30T Superior Quality Polypropylene Copolymer
- Borealis Visico™ LE4481/LE4437 Moisture-Crosslinking Polyethylene Compound for Flexible Low Voltage Insulation
- Lubrizol ESTANE® GP70AE Ester Based Thermoplastic Polyurethane (European Grade)
- Eurotec® Tecotek® BC40 UF65 NL CE PC/ABS, unfilled, heat & UV stabilized, natural, standard grade
- Wellman Wellamid® XT1863-BK1 Impact Modified Nylon 66
- ExxonMobil Exceed™ 3527PA Metallocene Polyethylene Resin