Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.00 - 10.0 GPa | 1160 - 1450 ksi | Injection; ISO 178 |
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
Flexural Modulus | 8.00 - 10.0 GPa | 1160 - 1450 ksi | Compression; ISO 178 |
Raschig Group 6501 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Flexural Modulus | 8.00 - 10.0 GPa | 1160 - 1450 ksi | Compression; ISO 178 |
Raschig Group 6551 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Flexural Modulus | 8.00 - 10.0 GPa | 1160 - 1450 ksi | Injection; ISO 178 |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
Flexural Modulus | 5.00 - 10.0 GPa | 725 - 1450 ksi | ASTM D790 |
Raschig Group PiMC 1221 High gloss PiMC is a Powder in-Mould Coating designed to improve the surface quality, durability and aesthetic appearance of SMC/BMC products. The PiMC is electro statically sprayed onto the heated mould surfa.. |
|||
Flexural Modulus | 5.00 - 10.0 GPa | 725 - 1450 ksi | ASTM D790 |
Raschig Group PiMC 1241 Sanitary, uni color PiMC is a Powder in-Mould Coating designed to improve the surface quality, durability and aesthetic appearance of SMC/BMC products. The PiMC is electro statically sprayed onto the heated mould surfa.. |
|||
Flexural Modulus | 5.00 - 10.0 GPa | 725 - 1450 ksi | ASTM D790 |
Raschig Group PiMC 1249 Sanitary, mix color PiMC is a Powder in-Mould Coating designed to improve the surface quality, durability and aesthetic appearance of SMC/BMC products. The PiMC is electro statically sprayed onto the heated mould surfa.. |
|||
Flexural Modulus | 5.00 - 10.0 GPa | 725 - 1450 ksi | ASTM D790 |
Raschig Group PiMC 1949 Granite colors PiMC is a Powder in-Mould Coating designed to improve the surface quality, durability and aesthetic appearance of SMC/BMC products. The PiMC is electro statically sprayed onto the heated mould surfa.. |
|||
Flexural Modulus | 7.00 - 10.0 GPa | 1020 - 1450 ksi | Injection; ISO 178 |
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
Flexural Modulus | 8.00 - 10.0 GPa | 1160 - 1450 ksi | Injection; ISO 178 |
Raschig Group RALUPOL® 2200 UP Polyester Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets.. |
|||
Flexural Modulus | 3.20 - 10.0 GPa | 464 - 1450 ksi | Average value: 5.62 GPa Grade Count:178 |
Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled". Specific grades with glass content between 15.. |
|||
Flexural Modulus | 4.14 - 10.0 GPa | 600 - 1450 ksi | Average value: 7.29 GPa Grade Count:44 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Flexural Modulus | 3.30 - 10.0 GPa | 479 - 1450 ksi | Average value: 6.65 GPa Grade Count:11 |
Overview of materials for Nylon 66/Nylon 6 Blend, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/Nylon 6 Blend, Glass Fiber Filled". Each property range of values reported is minimum and maxim.. |
|||
Flexural Modulus | 7.00 - 10.0 GPa | 1020 - 1450 ksi | DIN 53457 |
Schwartz Technical Plastics LAMINEX® 2101 Cotton Fabric, Phenolic Resin Impregnated Application: bearing segments and prismatic bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Modulus | 7.00 - 10.0 GPa | 1020 - 1450 ksi | DIN 53457 |
Schwartz Technical Plastics LAMINEX® 2141 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled Application: bearing segments and prismatic bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Modulus | 8.00 - 10.0 GPa | 1160 - 1450 ksi | ISO 178 |
Vyncolit 4221 XB Novolac Phenolic Mineral and organic filled phenolic molding compound with good mechanical properties.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Flexural Modulus | 7.00 - 10.0 GPa | 1020 - 1450 ksi | ASTM D790 |
Chang Chun Plastic PBT3030 30% Glass Fiber Enforced PBT Information provided by Dowell Trading Company Ltd. |
|||
Flexural Modulus | 7.00 - 10.0 GPa | 1020 - 1450 ksi | ASTM D790 |
Chang Chun Plastic PBT4830 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |
|||
Flexural Modulus | 7.00 - 10.0 GPa | 1020 - 1450 ksi | ASTM D790 |
Chang Chun Plastic PBT4130 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |
|||
Flexural Modulus | 0.228 - 10.0 GPa | 33.0 - 1450 ksi | Average value: 2.35 GPa Grade Count:391 |
Overview of materials for Polycarbonate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Molded". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Flexural Modulus | 3.45 - 10.0 GPa | 500 - 1450 ksi | Average value: 5.27 GPa Grade Count:18 |
Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% a.. |
|||
Flexural Modulus | 3.00 - 10.0 GPa | 435 - 1450 ksi | Average value: 5.60 GPa Grade Count:18 |
Overview of materials for Polystyrene + Polyphenylene Ether, Glass Filler This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene + Polyphenylene Ether, Glass Filler". Each property range of values reported is minimum and .. |