Polymer Property : Flexural Modulus = 493 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 3.40 GPa

@Temperature 23.0 °C
493 ksi

@Temperature 73.4 °F
ISO 178
Polykemi AB SCANMID 6 B12^ NH11L Nylon 6, Flame Retardant, Halogen Free
Information provided by Polykemi AB
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 3441R PC (Europe-Africa-Middle East)
Lexan 3441R is a medium viscosity, 10% glass reinforced polycarbonate grade, compliant with European food contact regulation EC Directive 2002/72/EC. The grade is especially designed for application..
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 500ECR PC
Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 500ECR PC (Asia Pacific)
Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Flexural Modulus 3.40 GPa
493 ksi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BFL2010 PC
Non-brominated, non-chlorinated flame retardant, glass reinforced PC with improved flow. Available in opaque colors.
Flexural Modulus 3.40 GPa
493 ksi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BFL2010 PC (Asia Pacific)
Non-brominated, non-chlorinated flame retardant, glass reinforced PC with improved flow. Available in opaque colors.
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® ML7667 PC Copolymer (Asia Pacific)
Lexan* ML7667 specialty polycarbonate (PC) resin is a 9% GF reinforced, UV stabilized, flame retarded injection molding grade. This medium flow specialty PC resin combines UL94 V0 @ 1.5mm, 5VB @ 3..
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® ML7667 PC Copolymer (Europe-Africa-Middle East)
Lexan* ML7667 specialty polycarbonate (PC) resin is a 9% GF reinforced, UV stabilized, flame retarded injection molding grade. This medium flow specialty PC resin combines UL94 V0 @ 1.5mm, 5VB @ 3..
Flexural Modulus 3.40 - 22.8 GPa
493 - 3300 ksi
Average value: 6.30 GPa Grade Count:20
Overview of materials for Polyphthalamide (PPA), Aramid Fiber
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Aramid Fiber". Each property range of values reported is minimum and maximum values of ..
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® HF500R PC (Europe-Africa-Middle East)
LEXAN HF500R is an easy flow, 9% glass reinforced, flame retardant grade, especially designed for applications requiring high rigidity together with high heat resistance and impact performance.
Flexural Modulus 3.40 - 9.32 GPa
493 - 1350 ksi
Average value: 6.32 GPa Grade Count:16
Overview of materials for PBT + ASA Blend, Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "PBT + ASA Blend, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum ..
Flexural Modulus 3.40 GPa
493 ksi
ISO 178
Mitsubishi Xantar® G2F 23 R Polycarbonate-10% Glass Reinforced
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Flexural Modulus 3.40 GPa
493 ksi
Conditioned; ISO 178
Lanxess Durethan® BKV 325 Z H2.0 901510 Nylon 6, 25% Glass Fibers
PA 6, 25% glass fibers, blow molding, impact modified, heat-ageing stabilized
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Lubricomp WFL32 PBT (Europe-Africa-Middle East)
LNP* Lubricomp* WFL32 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus 3.40 GPa
493 ksi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 4001 PEI
PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
Flexural Modulus 3.40 GPa
493 ksi
ISO 178
Solvay Specialty Polymers Ryton® QC160P Polyphenylene Sulfide (PPS)
Ryton® QC160P (pelletized) polyphenylene sulfide exhibits excellent thermal stability and chemical resistance and is suitable for thermoplastic extrusion processes.Features: Good Chemical Resista..
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Noryl GTX GTX8110 PPE+PA (Europe-Africa-Middle East)
GTX8110 is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaksThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Noryl GTX GTX8110P PPE+PA (Europe-Africa-Middle East)
GTX8110P is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaksThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus 3.40 GPa
493 ksi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Asia Pacific)
PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including wate..
Flexural Modulus 3.40 GPa
493 ksi
ASTM D790
Chase Plastics CP Pryme® N320GL (COND, 50% RH) Nylon 6 (Utility Grade), 20% Glass Fiber Reinforced, Internally Lubricated
Information provided by Chase Plastics.
Flexural Modulus 3.40 GPa
493 ksi
ASTM D790
A. Schulman POLYFORT™ FPP 1220 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
DescriptionPolyfort® FPP 1220 is a 20% glass filled chemically coupled impact copolymer polypropylene product.Information provided by A. Schulman.
Flexural Modulus 3.40 - 4.60 GPa
493 - 667 ksi
Average value: 4.20 GPa Grade Count:3
Overview of materials for PEKK, Unreinforced
This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate..
Flexural Modulus >= 3.40 GPa
>= 493 ksi
ASTM D790
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Flexural Modulus 3.40 GPa
493 ksi
ASTM D790
A. Schulman POLYFORT™ FPP 1220 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
DescriptionPolyfort® FPP 1220 is a 20% glass filled chemically coupled impact copolymer polypropylene product.Information provided by A. Schulman.
Flexural Modulus 3.40 GPa
493 ksi
ASTM D790
Ashley Polymers Ashlene® P291WO PPO
A reinforced, flame retardant resin with outstanding structural strength. Good appearance and high impact.Data provided by the manufacturer
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® EXL5689 PC Copolymer
Lexan* EXL5689 polycarbonate (PC) resin is a GF reinforced, UV stabilized, flame retardant injection molding copolymer blend. This medium flow resin features UL94 V0 @ 1.5mm flame retardancy based ..
Flexural Modulus 3.40 - 11.7 GPa
493 - 1700 ksi
Average value: 7.81 GPa Grade Count:22
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled". Each property range of values reported is ..