Polykemi AB SCANMID 6 B12^ NH11L Nylon 6, Flame Retardant, Halogen Free
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Polykemi AB |
| Trade Name | SCANMID 6 |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANMID 6 B12^ NH11L Nylon 6, Flame Retardant, Halogen Free.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | With Flow; ISO 2577 |
| 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 @Time 15.0 sec |
80 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 78.0 MPa | <= 11300 psi | ISO/R527 |
| Elongation at Break | 10 % | 10 % | ISO/R527 |
| Flexural Strength | <= 114 MPa | <= 16500 psi | ISO 178 |
| Flexural Modulus | 3.40 GPa @Temperature 23.0 °C |
493 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 197 °C @Load 5.001 kg |
387 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 213 °C @Load 1.00 kg |
415 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Glow Wire Test | 850 °C @Thickness 0.800 mm |
1560 °F @Thickness 0.0315 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant (discontinued **)
- IBC Advanced Alloys Beralcast® 363 Beryllium-Aluminum Alloy
- Seals Eastern Perflas® 9294 Perfluorinated Rubber
- SABIC Innovative Plastics ULTEM XH6050M PEI Copolymer (Asia Pacific)
- Valley Adhesives EM-500 High Temperature Application Glue Stick
- Zeon Chemicals Hydrin® H1100 Polyepichlorohydrin Elastomer
- Hexcel® HexWeb® CR III 3/8-5052-.0015 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Dow DOWLEX™ 2042A Linear Low Density Polyethylene, Food Grade
- Beijing Chemical Industry KAIFA® MN201-G20 Nylon 66 Resin
Copyright © lookpolymers.com All Rights Reserved