- SABIC Innovative Plastics Noryl GTX GTX8110P PPE+PA (Europe-Africa-Middle East)
SABIC Innovative Plastics Noryl GTX GTX8110P PPE+PA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GTX GTX8110P PPE+PA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GTX8110P is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaksThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 280 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 53.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
29.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
40.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Vicat Softening Point | 225 °C | 437 °F | Rate B/50; ISO 306 |
| 225 °C | 437 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EMB405LU Polyvinyl Chloride, Flexible (PVC, Flexible)
- Karina 750-DM-48/1-B-IS Black PVC Compound
- LyondellBasell Hostacomâ„¢ BG749GC/1 Polypropylene Copolymer
- SABIC Innovative Plastics NORYL NH5120 PPE+PS
- Chengdu Polyster KP-200-50 Silicone Masterbatch
- Fainplast Compounds CL 64/1 Flexible PVC, Sheathing
- 3M 4380 General Purpose Aluminum Foil Tape
- Parker Chomerics CHO-SHIELD® 2002 Conductive Coating
- Park Electrochemical Nelco® N4000-12 High Speed/Low Loss, CAF Resistant Laminate and Prepreg
Copyright © lookpolymers.com All Rights Reserved