Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.79 GPa | 405 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
Network Polymers MS 130HF Styrene Methyl Methacrylate Terpolymer Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics GELOY FXW749SK ASA Sparkle VisualFx ASA Resin - Weatherable |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
Quadrant EPP Quadrant Nylon 612 |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | 6.4 mm; ASTM D790 |
SABIC Innovative Plastics Lexan® FL903 PC Various weight reductions at 0.250"" (6.35 mm). High heat/creep resistance, excellent impact, flexural strength/rigidity. UV-stabilized. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | 6.4 mm; ASTM D790 |
SABIC Innovative Plastics Lexan® FL900 PC (Asia Pacific) Various weight reductions at 0.250"" (6.35 mm). High heat/creep resistance excellent impact, flexural strength/rigidity. UL94 V-1 at .157"" (3.99 mm). |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N2000HL Nylon 6 (DAM) Information provided by Ravago. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
PolyOne Geon™ Vinyl Fittings 210(HS) Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | 6.4 mm; ASTM D790 |
SABIC Innovative Plastics Lexan® FL900 PC Lexan* resin FL900 is a Br- & Cl-free flame retardant grade that can be foamed for weight reductions. UL-94 V1 listed at 3.9mm together with good stiffness, heat, creep and impact performance make i.. |
|||
Flexural Modulus | 2.79 GPa @Thickness 3.20 mm |
405 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical HT700 ABS, High Stiffness Feature: Injection Molding, High StiffnessApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Modulus | 2.79 GPa @Thickness 3.20 mm |
405 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY SG5009F PC/ABS Description: Injection Molding, PC/ABS, High Gloss, Scratch Resistance, Halogen Free Flame RetardantApplication: IT&OA (Notebook PC & Monitor housing)CAS: 103598-77-2 and 181028-79-5Information prov.. |
|||
Flexural Modulus | 2.79 GPa @Thickness 3.20 mm |
405 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY SG5009FA PC/ABS/PMMA, Halogen Free Flame Retardant Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, High Gloss, Anti-scratchApplication: IT&OA (Notebook PC housing)CAS: 103598-77-2, 9003-56-9, 9011-14-7 and 181028-79-5Informatio.. |
|||
Flexural Modulus | 2.79 GPa @Thickness 3.20 mm |
405 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical XG569C MABS, Anti-Scratch, High Gloss Feature: Injection Molding, Anti-Scratch, High GlossApplication: LCD TV Front Cabinet, Bezel, Audio/Video HousingCSA No. 9011-14-7 and 9003-56-9Information provided by LG Chemical |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp OP005XXC PPS LNP LUBRICOMP* OP005XXC is a compound based on Polyphenylene Sulfide resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-.. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OP005XXC PPS - LINEAR LNP LUBRICOMP* OP005XXC is a compound based on PPS - Linear resin containing 25% PTFE/Silicone. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OP005XXC PPS (Asia Pacific) LNP* LUBRICOMP* OP005XXC is a compound based on Polyphenylene Sulfide resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific) LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
Samyang Tramid® 210P Polyamide, High Productivity Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210P is a high productivity grade.Applications:ConnectorsCable tiesHarness clipsT.. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
Teknor Apex Chemlon® 100 L Nylon 66, Unreinforced Notes: Internally and externally lubricated; General Purpose; Double-lubricated for improved part ejection and machine feed Processing Method: Injection Molding Forms: PelletsInformation Provided by.. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON 9X02785 PC LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D-790 |
Axiall ProTherm® 4526 CPVC Rigid PVC, Molding Georgia Gulf ProTherm® 4526 CPVC is a pelletized injection molding compound designed for fittings. Typical applications are in potable water and chemical transfer systems especially where high res.. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
Asahi Kasei Tenac®-C EF750 Acetal Copolymer, Antistat
(discontinued **) Antistatic grade containing special carbon black.Applications: Parts requiring antistatic properties.This product is not a part of the standard product line dated 2003. |
|||
Flexural Modulus | 2.79 GPa | 405 ksi | |
Abatron AboCast 50-11/AboCure 50-12 Epoxy Information provided by Abatron, Inc.Processing: Shelf life: 12+ months (unmixed). 100/13.5 ratio. Pot life: 500 g, 36 min. at 25°C (77°F). Exothermic Peak 265°C (510°F). Hardens in 2-24 hou.. |