Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Kolon KOCETAL® TF302 Wear Modified Acetal Resin PTFE powder added, improved wear property. Applications: High speed, high load and wear resistant products. Information provided by API-Kolon. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
LG Chemical Lupox® GP1000H PBT Description: Injection Molding, PBT, High Flow, High ImpactApplication: Automotive (Connector)CAS No. 155123-66-3 and 24968-12-5Information provided by LG Chemical |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
5mm/min; ASTM D790 |
LG Chemical Lupox® TE5000G PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional Stability, Good WeatherabilityApplication: Automotive (Door Garnish, Door Handle)CAS No. 24968-12-5 and 103598-77-2Information provid.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
LG Chemical LUPOY HR-5007AX Heat Resistant PC/ABS Alloy, Unreinforced Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical SH610A ABS, High Impact Feature: Extrusion Molding, General Purpose, High ImpactApplication: Bag, Automobile InteriorCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical SH610S ABS, Excellent Surface, High Impact Feature: Extrusion Molding, Excellent Surface, High ImpactApplication: Bag, miscellaneousCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
5mm/min; ASTM D790 |
LG Chemical Lupox® TE5000GH PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional StabilityApplication: Automotive (Door Garnish)CAS No. 24968-12-5 and 103598-77-2Information provided by LG Chemical |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® 1102 PBT+PC Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Xylex X7200 PC+POLYESTER (Asia Pacific) General purpose, UV stabilised Xylex gradeThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Xylex X7200MR PC+POLYESTER (Asia Pacific) Mold Release version of X7200This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® WR-9370 ASA, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SD-0150AT ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® TX-0520 TRABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® VE-0860SE ABS, Unreinforced FR Flame-retardant ABS material that can be used in the exterior of adaptors, chargers etc.Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® WR-9100 ASA, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Samyang Trirex® 3030IR Polycarbonate TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D 790 |
SABIC Innovative Plastics Noryl INT1000 PPE+HIPS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SP6489 9940 High Impact Polystyrene Characteristics High flow Good toughness Available in black only Processing Injection moldingApplications TV and audio-video back and front cover Material Status: Commercial : ActiveAgency Ratings.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
PlastxWorld CEVIAN® E80 ABS Inherently Static Dissipative Transparent ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Wanshijie APET Sheet APET sheet is one of the earliest plastic sheets our company develops and produces. It has excellent air-tightness, durability, chemical resistance and transparency. When burnt, it will not produce .. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene DescriptionPolyfort® FPP 1902 HU is a 10% talc fortified polypropylene. It exhibits high flow and is stabilized for UV resistance. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene DescriptionPolyfort® FPP 1902 HU is a 10% talc fortified polypropylene. It exhibits high flow and is stabilized for UV resistance. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Braskem H 605 Thermoforming Polypropylene Applications: Flat and corrugated sheets with high transparency; thermoformed packing with high transparency. Information provided by Braskem |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Tipco Tipcolene® FX 6000 - UL94-V0 Flame Retardant & Mineral Reinforced Polypropylene Copolymer Mineral Reinforced V0 Flame Retardant PP CopolymerApplications: Modular SwitchesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Modulus | 1.96 - 5.47 GPa | 284 - 793 ksi | Average value: 2.44 GPa Grade Count:25 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Plating Grade". Each property range of values reported is minimum.. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SP 731 9920 High Impact Polystyrene Characteristics Speciality grade containing silicon oil to provide wear resistance and high opacity jet black color Easy flowing grade Processing Injection moldingApplications Camera parts Photogr.. |