| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WR-9370 ASA, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 46.1 MPa | 6680 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 65 % | 65 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 3.17 mm |
3.67 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- KB Alloys Tital® 10% Ti Titanium Aluminum Rod
- LyondellBasell Astryn 65F4-3 Polypropylene Homopolymer, 30% Talc
- LATI Latimass 62-07 D025 PA6, Impact Modified
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- ExxonMobil Mobilarma 247
- A. Schulman PP 1692 Polypropylene High Impact Copolymer
- Total Lumicene® mPE M 2735 S01 Metallocene Polyethylene, Cast Film
- DuPont Performance Polymers Crastin® S600LF NC010 PBT
- BASF 1-Vinylimidazole
- World Minerals Celite® Super Floss® MX Diatomaceous Earth Antiblock Additive
Copyright © lookpolymers.com All Rights Reserved