Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 15.0 GPa | 2180 ksi | |
Plastcom SLOVAMID 6 CF 20 PA6, 20% carbon fibre FeaturesChemically reinforced with 20 % carbon fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry... |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | STN EN ISO 178 |
Plastcom SLOVAMID 66 CF 20 Polyamide 66, 20% Carbon Fiber FeaturesChemically reinforced with 20% carbon fiber, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and electrical industry. .. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | |
Cookson Group Plaskon® 3400F Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A fast curing, reduced-stress epoxy molding compound for the encapsulation of semiconductor devices including DIPs, PLCCs, SOICs .. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
Solvay Specialty Polymers Ryton® R-4-200BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-200BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound developed to provide high strength, fast cycles, and low maintenance mol.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
Solvay Specialty Polymers Ryton® BR42B Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® BR42B is a 40% fiberglass reinforced polyphenylene sulfide compound specially formulated to have a low coefficient of friction for use in low surf.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
Solvay Specialty Polymers Ryton® R-4 02 Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4 02 is a 40% fiberglass reinforced polyphenylene sulfide compound which provides outstanding chemical resistance and mechanical properties even at elev.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | |
Lehmann & Voss LUVOCOM® 1105-7442 PEEK, with carbon fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts.High chemical resistance parts, hydrolysis resi.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | |
Lehmann & Voss LUVOCOM® 3/CF/30/EG Polyamide 6, with carbon fiber, extrusion grade Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressElectrically conductive, suitable.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific) LNP* Lubricomp* KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
Solvay Specialty Polymers Kalix® 9945 HFFR Polyamide, High Performance (HPPA), 45% Glass Fiber Kalix® 9945 HFFR is a 45% glass-fiber reinforced, halogen-free flame retardant High Performance Polyamide. It is hot-water moldable and intended for use in components requiring superior mechanica.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
Solvay Specialty Polymers Omnix® 9050 Polyamide, High Performance (HPPA), 50% Glass Fiber Omnix® 9050 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties even after moisture ab.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RX04031 PA 66 (Europe-Africa-Middle East) LNP* STARFLAM* RX04031 is a compound based on PA66 resin containing Carbon Fiber, Glass Fiber, Flame Retardant. Added features include: Non-Brominated & Non-Chlorinated Flame Retardant, Electricall.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp EF008E PEI LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp EF008E PEI (Asia Pacific) LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Asia Pac.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON RV00AESP PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AESP is a compound based on PA66 resin containing Long Glass Fiber. Added features include : Easy Molding, Heat Stabilized. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON RV00AESS PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AESS is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, Heat Stabilized. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON RV00AEX5 PA6.6 (Europe-Africa-Middle East) LNP* VERTON* Is a compound based on PA66 resin containing Long Glass Fiber. Added features include: Easy Molding, Heat Stabilized. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
Plenco 7556 Phenolic, Briquette, Injection Molded PLENCO 07556 is a glass fiber reinforced novolac phenolic molding compound, with good physical strengths and heat resistance along with excellent dimensional stability. UL recognized under component.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM-D790 |
Polyram PlusTek PA301G50 Nylon 6.6, Heat Stabilized, 50% Glass Fiber Heat stabilized, 50% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM-D790 |
Polyram PlusTek PA303G50 Nylon 6.6, 50% Glass Fiber 50% glass fiber reinforced, heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
Vyncolit X620/1 Novolac Phenolic Glass fiber and graphite filled phenolic molding compound with excellent friction properties.USES: Low friction bearings, video recorder and compact disc parts. Not suitable for applications requir.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
Covestro Baydur® STR/C-400 BB Polyurethane Composite SRIM Foam, 60% Glass Filled, MDI-based 2-Component Liquid System Contains directed chopped fiber preform glass.0.16 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bay.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | dry; ISO 178 |
DSM Stanyl® 46HF4550 PA46-GF50 50% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | 2 mm/min; ISO 178 |
Eurostar Staramide RF00AES PA66/6, 50% Glass Filled, Injection Molded Staramide RF00AES is a 50% Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66 C 50V S3)Information provided by Eurostar. |
|||
Flexural Modulus | >= 15.0 GPa | >= 2180 ksi | IEC 1212-2 5.2 |
Hippe EP GM 201 Glass Mat Reinforced Epoxy Resin - Sheet Used in mechanical and electrical applications. Extremely high mechanical strength at moderate temperature. Very good electrical properties under high humidity.Information provided by Hippe. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
BASF Ultramid® A3EG10 50% Glass Filled PA66 (Dry) Description: 50% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness as well as for electric insulating parts.Information provided by BASF |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
Resinoid 1322 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
LATI LARAMID G/45 45% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s.. |
|||
Flexural Modulus | 15.0 GPa | 2180 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON RX06097 PA 66 (Europe-Africa-Middle East) LNP* VERTON* RX06097 is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, UV-Stabilized. |