SABIC Innovative Plastics LNP Thermocomp EF008E PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp EF008E PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| 1.60 g/cc | 0.0578 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D 638 |
| 196 MPa | 28400 psi | ISO 527 | |
| Tensile Strength, Yield | 172 MPa | 24900 psi | ASTM D 638 |
| 175 MPa | 25400 psi | ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | ASTM D 638 |
| 4.7 % | 4.7 % | ISO 527 | |
| Elongation at Yield | 5.7 % | 5.7 % | ISO 527 |
| 7.5 % | 7.5 % | ASTM D 638 | |
| Tensile Modulus | 10.17 GPa | 1475 ksi | 1 mm/min; ISO 527 |
| 15.14 GPa | 2196 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D 790 |
| Flexural Modulus | 11.72 GPa | 1700 ksi | ASTM D 790 |
| 15.0 GPa | 2180 ksi | ISO 178 | |
| Izod Impact, Notched | 0.880 J/cm @Temperature 23.0 °C |
1.65 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 6.92 J/cm @Temperature 23.0 °C |
13.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² @Temperature 23.0 °C |
20.0 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 211 °C @Thickness 3.20 mm |
412 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- RheTech Products HP521-00UV 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Natural
- SABIC Innovative Plastics Lexan® 915RP PC (Asia Pacific)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N774 (SRF) Filler
- Shin-Etsu Silicones KMP-701 Fluid
- Covestro Makrolon® 2865 Polycarbonate, Flame Retardant Grade
- DuPont Performance Polymers Zytel® FN727 BK230A Nylon 6
- ACC EP AEP EPI Engineered Polymers
- Bostik 2128 Clear, Light Assembly EVA Glue Stick
- Asahi Glass AFLAS® SP TFE/P/VdF Fluoroelastomer
- Monmouth Rubber & Plastics Durafoam™ C19XLDS EPDM
Copyright © lookpolymers.com All Rights Reserved